一种耐磨合金钢及其制备方法技术

本发明专利技术提供了一种耐磨合金钢，其由以下成分组成：0.3～0.8wt％的C，0.3～0.9wt％的Si，0.3～1.1wt％Mn，1.5～6wt％的Cr，0.2～0.9wt％的Mo，0.3～1.2wt％的Ni，0～0.3wt％且不等于0的V，0～0.5wt％且不等于0的W，0～0.01wt％且不等于0的B，0～0.1wt％且不等于0的Ti，余量为Fe。本申请提供的耐磨合金钢通过调整合金元素的含量，并配合特定的热处理工艺，既保证了耐磨合金钢的硬度，又保证了其抗冲击性能，可以极大的提高板锤、甩锤、衬板等产品的使用寿命。

A wear-resistant alloy steel and its preparation method

The invention provides a wear-resistant alloy steel, which is composed of the following components: 0.3-0.8wt% C, 0.3-0.9wt% Si, 0.3-1.1wt% Mn, 1.5-6wt% Cr, 0.2-0.9wt% Mo, 0.3-1.2wt% Ni, 0-0.3wt% v, 0-0.5wt% w, 0-0.01wt% B, 0-0.1wt% Ti and 0 Fe. The wear-resistant alloy steel provided by the application can not only ensure the hardness of the wear-resistant alloy steel, but also ensure its impact resistance performance by adjusting the content of alloy elements and cooperating with specific heat treatment process, which can greatly improve the service life of plate hammer, throw hammer, lining plate and other products.

【技术实现步骤摘要】
一种耐磨合金钢及其制备方法
本专利技术涉及合金
，尤其涉及一种耐磨合金钢及其制备方法。
技术介绍
锤头、衬板、板锤、轧臼壁、磨辊、球磨机钢球以及棒磨机钢棒等配件是破碎机、制砂机、磨粉机或搅拌机等工业机械设备的主要磨损件，上述磨损件需要具有较好的耐磨性。目前，这些耐磨产品主要由高锰钢、合金钢或高铬铸铁等金属材料铸造而成，需要破碎的材料一般为矿石、石英砂、水泥等硬度相对较高的材料，这些磨损件承受冲击、挤压、剪切及接触疲劳的反复作用，工况条件恶劣，每年消耗大量的金属材料。因此，研制一种低成本、高硬度、高韧性的耐磨材料是一个迫切的问题。传统的耐磨材料中，高锰钢韧性最好，但初始硬度低(＜30HRC)，必须要有强大的冲击力才能产生加工硬化的作用来提高耐磨性，只适合冲击力很大的工况，而不适用于上述工况。高铬铸铁合金含量高，硬度可达到60HRC以上，而且组织内部含有硬度更高的碳化物，耐磨性非常好，但是冲击韧性很低，一般＜5J/cm2，也不适合上述冲击大的工况。合金钢硬度和韧性适中，一般冲击韧性为15～30J/cm2，硬度45～55HRC，本文档来自技高网...

【技术保护点】
1.一种耐磨合金钢，由以下重量百分比的成分组成：/n

【技术特征摘要】
1.一种耐磨合金钢，由以下重量百分比的成分组成：



S≤0.04％；
P≤0.04％；
余量为Fe。


2.根据权利要求1所述的耐磨合金钢，其特征在于，所述C的含量为0.35wt％～0.65wt％，所述Si的含量为0.6wt％～0.7wt％。


3.根据权利要求1所述的耐磨合金钢，其特征在于，所述Mn的含量为0.5wt％～0.8wt％，所述Cr的含量为1.8wt％～4.5wt％。


4.根据权利要求1所述的耐磨合金钢，其特征在于，所述Mo的含量为0.3wt％～0.5wt％，所述Ni的含量为0.5wt％～1.0wt％。


5.根据权利要求1所述的耐磨合金钢，其特征在于，所述V的含量为0.03wt％～0.2wt％，所述W的含量为0.1...

【专利技术属性】
技术研发人员：林迈里，张群力，熊碧军，李德海，熊志军，
申请(专利权)人：益阳金能新材料有限责任公司，
类型：发明
国别省市：湖南;43