The invention relates to a method for preparing graphene loaded with nanometer tungsten particles, which comprises the following steps: taking an appropriate amount of ammonium metatungstate, anhydrous glucose and NaCl, adding sufficient deionized water which can completely dissolve NaCl to obtain uniform and transparent precursor solution; freezing and drying to obtain dry solid powder, grinding to obtain mixed powder precursor; taking the powder obtained in the previous step The final precursor is calcined at high temperature under the protection of atmosphere, the atmosphere is hydrogen, the temperature is raised to 700 \u2011 780 \u2103, the temperature is kept for a period of time, and then the temperature is cooled to obtain the self-assembled powder of three-dimensional sodium chloride graphene loaded tungsten nanoparticles; the self-assembled powder prepared in the previous step is filtered with deionized water to remove NaCl, and then dried to obtain graphene loaded tungsten nanoparticles Powder.
【技术实现步骤摘要】
一种制备负载有纳米钨颗粒的石墨烯的方法
本专利技术属于纳米材料的制备
，具体涉及石墨烯的原位合成方法和在石墨烯上负载纳米金属颗粒的制备方法。技术背景石墨烯被发现以来，由于具有超高的力学性能、优良的导热导电性和较低的密度被广泛应用于结构材料和功能材料领域。就结构材料领域而言，石墨烯的理想抗拉强度达130GPa，弹性模量达1TPa，将其作为增强相应用于铜基、铝基或钛基等金属基复合材料中，能够极大的提高材料的强度和弹性模量，特别是石墨烯较低的密度，使其在增强轻质金属基复合材料的研究领域中具有重要的价值。然而，石墨烯在提高复合材料性能方面远远低于预期值，主要原因如下：第一，石墨烯之间存在较强的范德华力，导致石墨烯加入到金属基体中时容易发生团聚，难以均匀分散，而这种团聚的石墨烯在材料变形过程中极易在周围萌生裂纹，恶化材料性能；第二，石墨烯作为一种碳材料通常与金属基体具有较差的界面结合力，导致其在材料变形过程中难以承载载荷，有效发挥作用。针对以上问题，研究者们发现，在石墨烯上负载纳米金属颗粒，能够有效解决上述问题。原因...
【技术保护点】
1.一种制备负载有纳米钨颗粒的石墨烯的方法，包括下列步骤：/n(1)取适量的偏钨酸铵((NH
【技术特征摘要】
1.一种制备负载有纳米钨颗粒的石墨烯的方法，包括下列步骤：
(1)取适量的偏钨酸铵((NH4)6H2W12O40·XH20)、无水葡萄糖(C6H12O6)和NaCl，加入能够将NaCl全部溶解的足量去离子水，得到均一透明的前驱体溶液。
(2)将上一步制备的前驱体溶液冷冻干燥，得到干燥固体粉末，研磨后得到混合粉末前驱体；
(3)将上一步得到的粉末前驱体在气氛保护下高温煅烧，气氛为氢气，升温至700-780℃，保温一段时间，之后降温冷却，得到三维氯化钠-石墨烯负载钨纳米颗粒的...
【专利技术属性】
技术研发人员：何春年，徐志航，赵乃勤，师春生，沙军威，
申请(专利权)人：天津大学，
类型：发明
国别省市：天津;12
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。