The present disclosure provides a composition. In one embodiment, a composition i s provided and the composition comprises: (a) propylene polymer, the propylene polymer meeting the following requirements: (I) the density is 0.850g/cc to 0.900g/cc; and (II) the melt viscosity at 177 \u2103 is less than or equal to 10000mpa \u00b7 s; and (b) rosin ester, the rosin ester containing the following: (I) the total number of moles of carbon in the rosin ester is large Aliphatic carbon at or equal to 75 mol%; and (II) ester based carbon less than or equal to 3.0 mol% based on the total number of moles of carbon in the rosin ester.
【技术实现步骤摘要】
【国外来华专利技术】粘合剂组合物
技术介绍
在粘合剂行业中，通常使用氢化增粘剂调配单位点催化的聚烯烃弹性体用于热熔胶(HMA)以获得优异的粘合性能。然而，氢化增粘剂的生产成本高并且可能会随着石油原料供应紧张而供应紧张。松香类增粘剂(衍生自松香的增粘剂)是天然存在的并且成本低于氢化增粘剂。需要含有松香类增粘剂的新型粘合剂组合物，并且所述新型粘合剂组合物具有改进的聚烯烃弹性体与松香类增粘剂之间的相容性以及合适的粘合性能。此外，由于增粘剂供应短缺并且成本增加，因此对含有更高的聚合物含量和更少的增粘剂的HMA调配物的市场需求有所增长。然而，当使用传统增粘剂时，减少增粘剂的量并且增加聚合物的量具有HMA组合物的粘合性发生退化的缺点。在例如以下文献中公开了常规增粘剂：WO2015/013472；WO2016/028909；WO2016/029006；WO2016/029012；于2016年9月22日提交的国际申请第PCT/US2016/53040号；于2016年6月3日提交的美国临时申请第62/345,433号；和美国公开第2015/0018470号；JP2002526592；和JP200804513...
【技术保护点】
1.一种组合物，其包括以下：(A)丙烯类互聚物，所述丙烯类互聚物满足以下：(i)密度为0.850g/cc到0.900g/cc；并且(ii)在177℃下的熔体粘度小于或等于10,000mPa·s；以及(B)松香酯，所述松香酯包括以下：(i)按所述松香酯中的碳的总摩尔数计，大于或等于75mol％的脂肪族碳；和(ii)按所述松香酯中的碳的总摩尔数计，小于或等于3.0mol％的酯基碳。
【技术特征摘要】
【国外来华专利技术】1.一种组合物，其包括以下：(A)丙烯类互聚物，所述丙烯类互聚物满足以下：(i)密度为0.850g/cc到0.900g/cc；并且(ii)在177℃下的熔体粘度小于或等于10,000mPa·s；以及(B)松香酯，所述松香酯包括以下：(i)按所述松香酯中的碳的总摩尔数计，大于或等于75mol％的脂肪族碳；和(ii)按所述松香酯中的碳的总摩尔数计，小于或等于3.0mol％的酯基碳。2.根据权利要求1所述的组合物，其中按所述松香酯中的碳的总摩尔数计，所述松香酯包括75mol％到95mol％的脂肪族碳。3.根据权利要求1或权利要求2所述的组合物，其中按所述松香酯中的碳的总摩尔数计，所述松香酯包括0.5mol％到3.0mol％的酯基碳。4.根据权利要求1到3中任一项所述的组合物，其进一步包括丙烯类聚合物蜡，所述丙烯类聚合物蜡在170℃下的熔体粘度为40mPa·s到100mPa·s，并且密度为0.88g/cc到0.92g/cc。5.根据权利要求4所述的组合物，其中所述丙烯类互聚物与所...
【专利技术属性】
技术研发人员：L·张沃森，马万福，
申请(专利权)人：陶氏环球技术有限责任公司，
类型：发明
国别省市：美国,US