The invention discloses a geopolymer concrete with high strength and high carbonization resistance cured at room temperature and a preparation method thereof, including composite silica-alumina powder, composite alkali solution, fine aggregate, coarse aggregate, modified powder and water reducing agent. The invention takes fly ash and slag as composite silica-alumina powder, and adds modified powder (calcined hydrotalcite) to enhance the strength and carbonization resistance of geopolymer concrete, so as to ensure the normal construction of geopolymer concrete and meet the requirements of its safety and durability of building structure.
【技术实现步骤摘要】
常温养护高强高抗碳化性能的地聚物混凝土及其制备方法
本专利技术涉及建筑材料、土木工程技术，特别涉及一种常温养护高强高抗碳化性能的地聚物混凝土及其制备方法。
技术介绍
地质聚合物(简称地聚物)，是一种具有三维空间网状结构的类沸石水硬性无机聚合物材料，通过富含硅铝元素的原料与强碱发生解聚-缩聚反应而合成[1]。相对于普通硅酸盐水泥混凝土，由地聚物材料基体制备的地聚物混凝土，具有早期强度高、抗渗性能强、耐酸碱、耐高温、耐腐蚀、且与骨料几乎不发生碱集料反应等优点，因而近年来受到国内外学者的广泛关注。天然的硅铝质原料如高岭土及其煅烧产物偏高岭土，工业固废如粉煤灰、高炉矿渣、生物质灰等都可作为合成地聚物的原材料，其在常见的如(K)NaOH和(K)Na2SiO3等溶液中碱化并发生缩聚等一系列化学反应从而完成地聚物的制备。近年来，地聚物混凝土因其优良的性能而受到国内外学者们的大量研究。其制备过程免烧结，能耗低，三废排放量减少显著，符合节能环保的要求，同时能有效利用工业固废并改善区域生态环境，具有可观的经济和环境效应。但是相对于普通硅酸盐水泥混凝土，地聚物混凝土的抗碳化性能不理想[...
【技术保护点】
1.一种常温养护高强高抗碳化性能的地聚物混凝土，其特征在于，包括复合硅铝质粉料、复合碱溶液、细骨料、粗骨料、改性粉料和减水剂。
【技术特征摘要】
1.一种常温养护高强高抗碳化性能的地聚物混凝土，其特征在于，包括复合硅铝质粉料、复合碱溶液、细骨料、粗骨料、改性粉料和减水剂。2.根据权利要求1所述的一种常温养护高强高抗碳化性能的地聚物混凝土，其特征在于，按照质量百分比，所述复合硅铝质粉料：复合碱溶液中的固体成分：细骨料：粗骨料：改性粉料：减水剂＝1.00：0.23～0.25：1.5～2.0：1.5～4.0：0.02～0.08：0～0.05；所述复合碱溶液中的水成分与所述复合碱溶液中的固体成分和所述复合硅铝质粉料之和的比值为0.30～0.35。3.根据权利要求1所述的一种常温养护高强高抗碳化性能的地聚物混凝土，其特征在于，所述复合硅铝质粉料包括粉煤灰和高炉矿渣，按照质量百分比，所述粉煤灰：高炉矿渣＝1:0.67～4。4.根据权利要求3所述的一种常温养护高强高抗碳化性能的地聚物混凝土，其特征在于，所述粉煤灰为一级灰，粒径为0.1-100μm；所述高炉矿渣为S95级或S105级，粒径为0.1-100μm。5.根据权利要求1所述的一种常温养护高强高抗碳化性能的地聚物混凝土，其特征在于，所述复合碱溶液包括硅酸盐溶液、碱性固体颗粒和水；所述复合碱溶液的模数为1.2～1.5。6.根据权利要求5所述的一种常温养护高强高抗碳化性能的地聚物混凝土，其特征在于，所述硅酸盐溶液为液体硅酸钠、液体硅酸钾或液体硅酸钠和液体硅酸钾的组合，所述硅酸盐溶液的模...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。