The invention discloses a phenolic polyvinyl acetal resin adhesive and its preparation method. The product belongs to the chemical industry field. The raw materials used for producing the adhesive include: phenolic resin 20%22%, polyvinyl acetal resin 12%14%, styrene 50%, hexamethylenetetramine 4%, modified rosin resin 6%, fused quartz silica powder 3%, talc powder 3% by weight. The product is one. It has good mechanical properties, heat resistance, small shrinkage during hardening, good insulation, weather resistance, water resistance, aging resistance, film forming and impact resistance. It has good adhesion properties to glass, metal, wood, ceramics, leather, fibers and other materials.
【技术实现步骤摘要】
一种酚醛-聚乙烯醇缩醛树脂胶粘剂
：本专利技术产品属于化工建材领域，涉及一种酚醛-聚乙烯醇缩醛树脂胶粘剂及其制备方法。
技术介绍
：酚醛树脂具有良好的耐酸性能、力学性能、耐热性能，其重要应用之一就是制备胶粘剂，它和各种各样的有机和无机填料都能相容；单一的酚醛树脂胶粘剂具有良好力学性能、耐热性能、粘结力较强、化学稳定性好、硬化时收缩小，但有性脆、耐磨性较低、内应力大易老化龟裂等缺点，使其应用受到一定限制，必须进行改性，聚乙烯醇缩醛就是改性材料之一。聚乙烯醇与各种醛类的缩合产物的统称聚乙烯醇缩醛，主要品种是聚乙烯醇缩甲醛和缩丁醛两种，聚乙烯醇缩醛无毒、无臭、无腐蚀性，具有一定的化学稳定性，由它来对酚醛树脂进行改性，可使两种树脂的优良特性得到充分发挥，缺陷得到弥补，制得的胶粘剂具有良好力学性能、耐热性能、化学稳定性好、硬化时收缩小及良好的绝缘性、耐侯性、耐水性、耐老化性、成膜性和抗冲击性能，对玻璃、金属、木材、陶瓷、皮革、纤维等材料有良好的粘接性能。
技术实现思路
：本专利技术产品是一种酚醛-聚乙烯醇缩醛树脂胶粘剂,生产该胶粘剂使用的原料按重量配比包括：酚醛树脂20%-22%、聚乙烯醇缩醛树脂12%-14%、苯乙烯50%、六次甲基四胺4%、改性松香树脂6%、熔融石英硅微粉3%、滑石粉3%。本专利技术可以通过以下技术方案来实现：（1）将配方量的苯乙烯送入化学反应釜，升温至45-47℃，开动搅拌机搅拌，然后缓慢的加入配方量的酚醛树脂和配方量的聚乙烯醇缩醛树脂，混合后搅拌1.0-1.2小时。（2）降温至常温，继续搅拌，边搅拌边将配方量的六次甲基四胺、改性松香树脂、熔融石英...
【技术保护点】
1.一种酚醛‑聚乙烯醇缩醛树脂胶粘剂，生产该胶粘剂使用的原料按重量配比包括：酚醛树脂20%‑22%、聚乙烯醇缩醛树脂12%‑14%、苯乙烯50%、六次甲基四胺4%、改性松香树脂6%、熔融石英硅微粉3%、滑石粉3%，其特征是：（1）将配方量的苯乙烯送入化学反应釜，升温至45‑47℃，开动搅拌机搅拌，然后缓慢的加入配方量的酚醛树脂和配方量的聚乙烯醇缩醛树脂，混合后搅拌1.0‑1.2小时；（2）降温至常温，继续搅拌，边搅拌边将配方量的六次甲基四胺、改性松香树脂、熔融石英硅微粉、滑石粉送入化学反应釜，搅拌反应0.3‑0.4小时后得到成品。
【技术特征摘要】
1.一种酚醛-聚乙烯醇缩醛树脂胶粘剂，生产该胶粘剂使用的原料按重量配比包括：酚醛树脂20%-22%、聚乙烯醇缩醛树脂12%-14%、苯乙烯50%、六次甲基四胺4%、改性松香树脂6%、熔融石英硅微粉3%、滑石粉3%，其特征是：（1）将配方量的苯乙烯送入化学反应釜，升温至45-47℃，开动搅拌机搅拌，然后缓慢的加入配方量的酚醛树脂和配方量的聚乙烯醇缩醛树脂，混合后搅拌...
【专利技术属性】
技术研发人员：朱云利，
申请(专利权)人：新沂景尚建材有限公司，
类型：发明
国别省市：江苏,32