一种电极材料及其制备方法和应用技术

本发明专利技术涉及电极材料技术领域，尤其涉及一种电极材料及其制备方法和应用，本发明专利技术提供的电极材料，由包括以下重量份的原料制备得到：氧化锆30～50份，稳定剂0.1～15份，二氧化硅0～10份，氧化铝0～10份，碳纳米管10～30份、石墨烯10～30份和尼龙0.05～1.45份。根据实施例的记载，本发明专利技术所述的电极材料作为电极应用到Zeta电位仪中，电泳迁移率可达1.0×10

A kind of electrode material and its preparation method and Application

The invention relates to the technical field of electrode materials, in particular to an electrode material and its preparation method and application. The electrode materials provided by the invention are prepared from raw materials including 30-50 parts of zirconia, 0.1-15 parts of stabilizer, 0-10 parts of silica, 0-10 parts of alumina, 10-30 parts of carbon nanotubes, 10-30 parts of graphene and 0.05-1.45 parts of nylon. According to the description of the embodiment, the electrode material of the present invention is applied to the Zeta potentiometer as an electrode, and the electrophoretic mobility can reach 1.0*10.

【技术实现步骤摘要】
一种电极材料及其制备方法和应用
本专利技术涉及电极材料
，尤其涉及一种电极材料及其制备方法和应用。
技术介绍
测试仪器中的传统电极通常采用银、铂和钛等各种金属制成，如，公开号为CN101861412A的中国专利公开了一种电极，其包含：a)包含M(n+1)AXn的电极基材，其中M为元素周期表第IIIB、IVB、VB、VIB或VIII族的金属或其组合，A为元素周期表第IIIA、IVA、VA或VIA族的元素或其组合，X为碳、氮或其组合，其中n为1、2或3；和b)在所述电极基材上沉积的电催化涂层，其选自如下的至少一种：b.2)包含BfCgDhEi的金属氧化物，其中B为钌、铂、铑、钯和钴中的至少一种，C为至少一种阀金属，D为铱，E为Mo和/或W，其中f为0.35～1，g为0～1，h为0～1，i为0～0.5，其中f+g+h+i＝1。但是，该电极价格昂贵，易中毒失效，工作寿命短，是一台测试仪器中成本最高的更换配件之一。近年来，碳电极因为其材料纯度高，电阻率低，并在沉积条件下具有化学惰性，逐渐呈现了可替代金属电极的能力。公开号为CN103972521A的中国专利公开了一种电极，所述电极包括具有本文档来自技高网...

【技术保护点】
1.一种电极材料，由包括以下重量份的原料制备得到：

【技术特征摘要】
1.一种电极材料，由包括以下重量份的原料制备得到：2.如权利要求1所述的电极材料，其特征在于，由包括以下重量份的原料制备得到：3.权利要求1或2所述的电极材料的制备方法，包括以下步骤：将尼龙分散液与氧化锆、稳定剂、二氧化硅、氧化铝、碳纳米管和石墨烯混合，得到混合料；将所述混合料进行成型处理，得到电极材料。4.如权利要求3所述的制备方法，其特征在于，所述成型处理包括压制、预烧结和致密化。5.如权利要求4所述的制备方法，其特征在于，所述压制的压力为80～200MPa...

【专利技术属性】
技术研发人员：段兴汉，武桐，
申请(专利权)人：上海景瑞阳实业有限公司，
类型：发明
国别省市：上海,31