The invention discloses a preparation method of nitrogen-boron co-doped porous carbon composite material, which can obtain p-hydroxyphenylboric acid solution by dissolving p-hydroxyphenylboric acid in deionized water, mixing uniformly by magnetic stirring, and dropping amino cyanide solution and p-hydroxyphenylboric acid solution into deionized water at the same time under magnetic stirring, and mixing uniformly by magnetic stirring to obtain mixed solution. The white powders were obtained by freezing rapidly with liquid nitrogen and drying in a freeze dryer. The powders were calcined in an inert gas atmosphere to prepare nitrogen-boron co-doped carbon materials. The invention has the advantages of excellent electrochemical performance, simple preparation method and low cost.
【技术实现步骤摘要】
氮硼共掺杂多孔碳复合材料的制备方法
本专利技术涉及氮硼共掺杂多孔碳复合材料的制备方法，属于碳材料与锂离子二次电池
技术介绍
不可再生的化石能源大量的损耗以及环境问题已经成为当下的热点话题，例如二氧化碳的排放造成温室效应已经为人类敲响了警钟。随着经济、工业的不断进步，人口数量日益增多，生活需求日渐增高，人们对能源的索取已经临近供不应求，储量日渐贫乏。这迫使我们要寻找一种既安全又环保的新型能源来替代化石能源。绿色能源，例如太阳能，水力，热力以及风能终将代替传统能源。这些可再生能源中，太阳能和风能有一定的间歇性。锂离子电池的出现，解决了至关重要的问题，因此聚焦了不少科学家的关注，在近些年来也得到了突飞猛进的发展，锂离子电池由于具有高能力密度、高功率密度、长循环寿命和不污染环境等优势而成为新一代的高能绿色储能材料。目前，锂离子电池已经广泛应用于各类便携式电子产品、可穿戴电子产品和电动汽车等储能器件领域。为了满足当前对高能量密度、高功率密度和稳定的长循环寿命电极材料的急切需求，研究具有高理论比容量和低电压平台(负极)的电极材料迫在眉睫。对负极材料而言，当前商业化采...
【技术保护点】
1.一种氮硼共掺杂多孔碳复合材料的制备方法，其特征在于，所述制备方法包括：将适量对羟基苯硼酸以1:10质量比溶于去离子水中，搅拌1h使其混合均匀，得到对羟基苯硼酸溶液；将氨基氰和对羟基苯硼酸溶液按照体积比1:(0.2‑5)加入持续搅拌的适量去离子水中，搅拌1‑5h使其混合均匀，得到混合溶液；将混合溶液用液氮快速冷冻形成冷冻物，并将冷冻物放入冷冻干燥机中干燥36～60h，得到白色粉末；将惰性气体通入加热炉中形成惰性氛围，并将白色粉末放入所述加热炉中，使所述加热炉进行程序升温并使得白色粉末在所述加热炉中煅烧，得到氮硼共掺杂多孔碳复合材料。
【技术特征摘要】
1.一种氮硼共掺杂多孔碳复合材料的制备方法，其特征在于，所述制备方法包括：将适量对羟基苯硼酸以1:10质量比溶于去离子水中，搅拌1h使其混合均匀，得到对羟基苯硼酸溶液；将氨基氰和对羟基苯硼酸溶液按照体积比1:(0.2-5)加入持续搅拌的适量去离子水中，搅拌1-5h使其混合均匀，得到混合溶液；将混合溶液用液氮快速冷冻形成冷冻物，并将冷冻物放入冷冻干燥机中干燥36～60h，得到白色粉末；将惰性气体通入加热炉中形成惰性氛围，并将白色粉末放入所述加热炉中，使所述加热炉进行程序升温并使得白色粉末在所述加热炉中煅烧，得到氮硼共掺杂多孔碳复合材料。2.根据权利要求1所述的氮硼共掺杂多孔碳...
【专利技术属性】
技术研发人员：庞维琳，陈冬，李汉辰，
申请(专利权)人：北京碳极极电科技有限公司，
类型：发明
国别省市：北京,11