The invention provides an insulating and thermal conductive modified nylon 6 composite material, which is prepared by the following methods: 1) mixing PA6, high spherical alumina, nano silicon carbide and nano boron nitride as raw materials in a high-speed mixer for 3 minutes; 2) extruding and granulating by a twin screw extruder; after fully drying the granules, the insulating and thermal conductive modified nylon 6 composite material is obtained; and 2) the steps 1) are described. The contents of PA6, high sphericity alumina, nano-SiC and nano-boron nitride are 40 50, 45 55, 5 10 and 5 10 respectively. The insulating and thermal conductive modified nylon 6 composite material of the invention has insulating and thermal conductive properties.
【技术实现步骤摘要】
一种绝缘导热改性尼龙6复合材料
本专利技术涉及一种绝缘导热改性尼龙6复合材料,属于尼龙工程塑料
技术介绍
尼龙工程塑料以其在机械性能、耐久性、耐腐蚀性、耐热性等方面的高性能优势,被广泛应用于电子电气、汽车、建筑、办公设备、机械、航空航天等行业,以塑代钢、以塑代木已成为国际流行趋势。尼龙工程塑料作为当今世界塑料工业中增长速度最快的领域,其发展不仅对国家支柱产业和现代高新技术产业起着支撑作用,同时也推动传统产业改造和产品结构的调整。改性尼龙以尼龙原料为基料,加以改变其物理性质而形成的颗粒状产品。如:增强尼龙,增韧尼龙,耐磨尼龙,无卤阻燃尼龙,导电尼龙,阻燃尼龙等。随着集成技术、微电子封装技术和大功率LED技术的发展,电子元件和电子设备向小型化和微型化发展,电子设备所产生的热量迅速积累、增加。为保证电子元器件在使用环境温度下能高可靠性地正常工作,需要开发导热绝缘的材料。现有技术中还缺少一种绝缘导热改性尼龙6复合材料。
技术实现思路
本专利技术的目的是克服现有技术的不足,提供一种绝缘导热改性尼龙6复合材料。本专利技术的技术方案如下:一种绝缘导热改性尼龙6复合材料,采用如下方法制备而成:1)以PA6、高球形度氧化铝、纳米碳化硅和纳米氮化硼为原料,在高速混合机中混合3min;2)经双螺杆挤出机挤出造粒;将粒料充分干燥后,即得绝缘导热改性尼龙6复合材料;所述的步骤1)中,得到的混合料中,各原料含量如下:PA6的含量为40-50重量份,高球形度氧化铝为45-55重量份,纳米碳化硅的含量为5-10重量份,纳米氮化硼的含量为5-10重量份。优选地,所述的步骤1)中,得到 ...
【技术保护点】
1.一种绝缘导热改性尼龙6复合材料,其特征在于,采用如下方法制备而成:1)以PA6、高球形度氧化铝、纳米碳化硅和纳米氮化硼为原料,在高速混合机中混合3min;2)经双螺杆挤出机挤出造粒;将粒料充分干燥后,即得绝缘导热改性尼龙6复合材料;所述的步骤1)中,得到的混合料中,各原料含量如下:PA6的含量为40‑50重量份,高球形度氧化铝为45‑55重量份,纳米碳化硅的含量为5‑10重量份,纳米氮化硼的含量为5‑10重量份。
【技术特征摘要】
1.一种绝缘导热改性尼龙6复合材料,其特征在于,采用如下方法制备而成:1)以PA6、高球形度氧化铝、纳米碳化硅和纳米氮化硼为原料,在高速混合机中混合3min;2)经双螺杆挤出机挤出造粒;将粒料充分干燥后,即得绝缘导热改性尼龙6复合材料;所述的步骤1)中,得到的混合料中,各原料含量如下:PA6的含量为40-50重量份...
【专利技术属性】
技术研发人员:王进,
申请(专利权)人:南通瑞隆新材料有限公司,
类型:发明
国别省市:江苏,32