The invention discloses a novel high strength fully degradable polyester composite material and a preparation method thereof. The new polyester composite material consists of 10 to 80 parts of thermoplastic modified polyvinyl alcohol (TPVA), 10 to 80 parts of polylactic acid (PLA), 0 to 2 parts of compatibilizer, 0 to 0.5 parts of antioxidant and 0 to 1.5 parts of antioxidant. The preparation method of the novel polyester composite comprises the following steps: (1) preparation of TPVA; (2) preparation of the novel polyester composite. The invention provides a novel high strength fully degradable polyester composite material, which overcomes the problem of product performance degradation in the traditional processing process based on PVA aqueous solution, and the product obtained has excellent mechanical properties.
【技术实现步骤摘要】
一种高强度全降解新型聚酯复合材料及其制备方法
本专利技术涉及可降解高分子材料领域与水体净化领域，具体地，涉及一种高强度全降解新型聚酯复合材料及其制备方法。
技术介绍
近几年，全球每年生产的塑料超过3亿，其中每年约产生800万吨塑料垃圾通过被直接丢弃、暴风雨冲刷以及内陆河道垃圾顺流等直接或间接方式进入海洋，并且通过洋流使它们广泛存在于整个海洋生态系统中。这些塑料垃圾一部分停留在海滩上，一部分漂浮在海面或沉入海底，严重破坏海洋生态环境，影响海上交通正常运作，危害海洋生物多样性。同时，海洋垃圾通过漫长的食物链对人类造成间接而严重的危害。目前已有报道在人体内检测出了塑料成分。为了使废弃塑料进入海水后能够降解，很多水溶性高分子材料满足这一条件。但要使材料能在水体环境中进行降解，并且降解后的产物为对环境无危害的小分子，且同时满足材料制品在使用周期中对使用强度的要求。基于以上考虑，热塑性改性聚乙烯醇/聚乳酸聚酯复合体系可以很好地满足上述要求，其可在污水污泥、河水、海水等环境中完全降解，且降解周期和使用周期可通过改变组分质量比例进行调控。但该聚酯复合材料在实际应用中存在力学性能较...
【技术保护点】
1.一种高强度全降解新型聚酯复合材料，其特征在于由以下重量份数的原料制成：热塑性改性后的聚乙烯醇10‑80份；聚乳酸10‑80份；相容剂0‑2份；抗氧剂0‑0.5份；防老剂0‑1.5份。
【技术特征摘要】
1.一种高强度全降解新型聚酯复合材料，其特征在于由以下重量份数的原料制成：热塑性改性后的聚乙烯醇10-80份；聚乳酸10-80份；相容剂0-2份；抗氧剂0-0.5份；防老剂0-1.5份。2.根据权利要求1所述的高强度全降解新型聚酯复合材料，其特征在于，所述热塑性改性聚乙烯醇是通过将聚乙烯醇与改性剂共混，经密封塑化挤出造粒可得。3.根据权利要求2所述的高强度全降解新型聚酯复合材料，其特征在于，所述改性剂为己内酰胺与六水合氯化镁的复合体系，其中己内酰胺、六水合氯化镁与聚乙烯醇的质量比为2.1∶2∶100-2.1∶2∶150。4.根据权利要求1所述的高强度全降解新型聚...
【专利技术属性】
技术研发人员：张金泉，刘天赐，杭祖圣，费韦多，董铁男，戴清文，宗敬东，曹玺，李佩芬，吴玉成，
申请(专利权)人：南京工程学院，南京立汉化学有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。