The present invention relates to a method for recovering the performance of zinc bromide single liquid flow battery. The positive electrolyte is filled in the positive chamber of the battery, and the negative electrolyte stored in the negative storage tank circulates through the pipeline between the negative storage tank and the negative chamber of the battery. After a period of operation of the battery, the positive electrolyte in the positive chamber is introduced into the negative storage tank and mixed with the negative electrolyte. A part of the mixed solution was filled into the positive chamber again, and the performance of the battery was restored by mixing the positive and negative electrolytes. The invention provides a method for recovering the performance of zinc bromide liquid flow battery when its performance decreases, solves the problem of efficiency attenuation during the operation of zinc bromide liquid flow battery, and improves the service life of the battery.
【技术实现步骤摘要】
一种锌溴单液流电池性能的恢复方法
本专利技术涉及一种电池性能恢复方法在锌溴液流电池中的应用。
技术介绍
风能、太阳能等可再生能源具有不连续、不稳定的特点，其这一特性会使其在并网过程中对电网造成冲击，影响电网安全稳定运行。储能技术则可以保证可再生能源发电并网的高效稳定运行。储能技术主要分为物理储能和化学储能两大类。化学储能中适用于大规模、大容量储能的氧化还原液流电池因其具有电池功率和容量相互独立、响应迅速、结构简单、易于设计等优点而受到广泛关注。锌溴液流电池作为氧化还原液流电池的一种，除具有上述优点外，还具有高开路电压(1.85V),高理论能量密度(435Wh/Kg),电解液、隔膜价格低廉等诸多优势。这些优势也使其与其它液流电池相比更具竞争力。锌溴液流电池在充放电运行过程中存在负极锌的累积的问题，而锌的累积会使电池极化变大造成电池性能衰减，影响电池使用寿命，严重情况下甚至会形成枝晶造成电池短路失效。因此，解决负极锌的累积问题对提高电池使用寿命，保障电池稳定运行具有重要作用。
技术实现思路
：本专利技术目的在于解决上述问题，提供了锌溴液流电池电池性能恢复的方法，通过正负极...
【技术保护点】
1.一种锌溴单液流电池性能的恢复方法，电池的正极腔室内填充有正极电解液，储存于负极储罐内的负极电解液经管路在负极储罐和电池的负极腔室间循环流动，其特征在于：在电池运行一段时间后，将正极腔室内的正极电解液导入负极储罐内与负极电解液混合，然后将部分混合液再次填充至正极腔室内，通过正负极电解液互混使电池性能恢复。
【技术特征摘要】
1.一种锌溴单液流电池性能的恢复方法，电池的正极腔室内填充有正极电解液，储存于负极储罐内的负极电解液经管路在负极储罐和电池的负极腔室间循环流动，其特征在于：在电池运行一段时间后，将正极腔室内的正极电解液导入负极储罐内与负极电解液混合，然后将部分混合液再次填充至正极腔室内，通过正负极电解液互混使电池性能恢复。2.根据权利要求1所述应用，其特征在于：电池运行一段时间后，当电池能量...