The invention discloses a smelting method for increasing scrap ratio by preheating scrap steel in converter. The method is as follows: the scrap steel ratio is controlled in the burden structure from 24% to 27%, and the molten iron ratio is controlled from 73% to 76%. The scrap steel is added to scrap steel hopper first, then the scrap steel hopper is transferred to the coal feeding span, and 9-12kg/t anthracite is added to the scrap steel hopper, and then the scrap steel hopper is transferred to the front of the converter and added to the converter. In the converter, the scrap is preheated by oxygen blowing from oxygen lance, and the oxygen blowing capacity is controlled in the range of 10.0-12.2Nm.
【技术实现步骤摘要】
一种转炉预热废钢提高废钢比的冶炼方法
本专利技术属于钢铁冶金领域，具体涉及一种转炉预热废钢提高废钢比的冶炼方法。
技术介绍
废钢作为钢铁工业的绿色资源，具有较高的载能环保价值。随着我国钢铁工业的迅速发展，我国的钢铁量逐年增加，同时社会废钢资源也相应的增长。国家明确表示全面取缔生产“地条钢”的中频炉、工频炉产能，将在短时间内推高我国钢铁工业的废钢供应量。社会废钢资料充足，价格相对铁水更有竞争力，在此情况下，提高转炉炼钢废钢比，不仅可提高炼钢产量，还能降低炼钢成本。转炉提高废钢比冶炼主要需解决炉内热源不足的问题，现有提高转炉炼钢废钢比的技术主要有以下两种：第一种是转炉冶炼过程添加升温材料(碳系、硅系或铝系)，可增加炉内热源，提高废钢比，但此方法容易增加钢水中的S、N等杂质元素，且升温剂的热效率相对较低；第二种是炉外预热废钢，如铁水包烘烤废钢或废钢在感应炉中加热等，此种方式需额外增添设备，且增大调度难度。综上所述，寻找一种操作便捷、成本低廉的提高吨钢废钢比的冶炼方法，是当前冶金工作者急需解决的问题。
技术实现思路
为克服转炉高废钢比冶炼出现的热量不足的问题，本专利技术提供一...
【技术保护点】
1.一种转炉预热废钢提高废钢比的冶炼方法，包括装料、废钢预热、加铁水冶炼及出钢，其特征在于：(1)装料：将废钢和无烟煤加入转炉炉内，无烟煤加入量为9～12kg/t，炉料结构中废钢比控制在24％～27％，(2)废钢预热：下氧枪吹氧预热废钢，吹氧量控制在10.0～12.2Nm
【技术特征摘要】
1.一种转炉预热废钢提高废钢比的冶炼方法，包括装料、废钢预热、加铁水冶炼及出钢，其特征在于：(1)装料：将废钢和无烟煤加入转炉炉内，无烟煤加入量为9～12kg/t，炉料结构中废钢比控制在24％～27％，(2)废钢预热：下氧枪吹氧预热废钢，吹氧量控制在10.0～12.2Nm3/t，废钢预热完之后提枪并来回摇炉；(3)兑铁水冶炼：摇炉兑铁水，铁水加入量为总炉料的73％～76％，与废钢加入量相匹配，之后重新下氧枪吹炼，终点炉渣碱度控制在3.2～3.8；(4)出钢：当钢水的温度达到1620～1650℃，钢水中磷的质量分数小于0.015％，碳的质量分数为0.03％～0.08％时，进行出钢操作。2.根据权利要求1所述的转炉预热废钢提高废钢比的冶炼方法，其特征在于：所述...
【专利技术属性】
技术研发人员：管挺，黄永林，皇祝平，王耀，邹长东，刘飞，
申请(专利权)人：江苏省沙钢钢铁研究院有限公司，张家港宏昌钢板有限公司，江苏沙钢集团有限公司，
类型：发明
国别省市：江苏,32