The invention discloses a polymer hot melt adhesive and sealing gasket for glass container. Its composition and weight percentage are squalane 27.1-32.3%, ethylene-methyl methacrylate copolymer 17.6-22.1%, ethylene propylene terpolymer 9.2-11.6%, polylactic acid 9.3-13.3%, polyvinyl alcohol 12.3-13.6%, C9 petroleum resin 9.4-12.7%, amorphous propylene copolymer 4.2-5.3%. Because squalane is used to improve the adhesion, bonding strength, adjust the heat resistance temperature and drying time of hot melt adhesive powder, improve the operability and reduce the cost, ethylene-methyl methacrylate copolymer is used to improve the texture and odor, and ethylene propylene terpolymer is used to adjust the chemical corrosion resistance and solvent resistance. The sealing gasket of sealing glass containers has oil resistance, solvent resistance, water resistance and good sealing effect.
【技术实现步骤摘要】
高分子热熔胶及封玻璃容器封口垫片
本专利技术涉及化工胶粘剂
，特别是涉及一种高分子热熔胶及封玻璃容器封口垫片。
技术介绍
热熔胶粘剂(HotMeltAdhesive)简称热熔胶，通常是指在室温下呈固态，加热熔融成液态，涂布，润湿被粘物后，经压合、冷却，在几秒钟内完成粘接的胶粘剂。热熔胶是一类在室温下呈固态，加热熔融后呈液态，涂布于被粘物后，经压合、冷却，在短时间内即可完成粘接的胶粘剂。如图1所示，一种玻璃容器封口垫片，由粘封层、铝塑膜层和背衬层组成，所述铝塑膜层底面和背衬层顶面叠置复合，在铝箔层顶面上设置粘封层。大部分粘封层存在抗紫外线性能差的问题，经过紫外线污染后其初粘力、持粘力、剥离力以及残留均受到影响，粘封层耐油、耐溶剂、耐水性差，容易失去粘性，造成内容物不泄漏。
技术实现思路
本专利技术的一个目的在于提供一种高分子热熔胶。本专利技术的另一个目的在提供一种耐油、耐溶剂且耐水性的封玻璃容器封口垫片。为实现上述目的，本专利技术的技术解决方案是：本专利技术是一种高分子热熔胶，其组成和重量百分比为：角鲨烷36.4～43.9%乙烯—甲基丙烯酸甲酯共聚物17.6～22...
【技术保护点】
1.一种高分子热熔胶，其特征在于：其组成和重量百分比为：角鲨烷 36.4～43.9%乙烯—甲基丙烯酸甲酯共聚物 17.6～22.1%聚乳酸 9.3～13.2%聚乙烯醇 12.3～13.6%C9石油树脂 9.4～12.7%非晶态丙烯共聚物 4.2～5.3%。
【技术特征摘要】
1.一种高分子热熔胶，其特征在于：其组成和重量百分比为：角鲨烷36.4～43.9%乙烯—甲基丙烯酸甲酯共聚物17.6～22.1%聚乳酸9.3～13.2%聚乙烯醇12.3～13.6%C9石油树脂9.4～12.7%非晶态丙烯共聚物4...
【专利技术属性】
技术研发人员：杨严武，
申请(专利权)人：鼎贞厦门实业有限公司，
类型：发明
国别省市：福建,35