The waterproof coating is composed of 30 to 50% styrene acrylic acrylate copolymer acrylic emulsion, 25 to 30% stone powder, 0 to 5% heavy calcium, 1 to 5% antioxidants, 0 to 5% defoamers, 0 to 0 talcum powder, 0 to 5% gaseous phase silicon oxide, 12 to 10 polyvinyl alcohol, water glass of 0 to 9, and water of the mixture. The waterproof coating is waterproof, vapor-proof, strong adhesion and good film-forming hardness; adding antioxidant and defoamer, it is not easy to foam and anti-aging; stone powder is made of natural stone with considerable hardness, good mechanical properties, good adhesion and compactness; polyvinyl alcohol has anti-mildew and thickening effect.
【技术实现步骤摘要】
一种防水涂料
本专利技术涉及一种防水涂料,属于建筑建材
技术介绍
内外墙的涂料品种较多,尤其是高分子乳液材料的出现,为涂料的品种增添了许多新品种。其防水、抗氧化能力增强。然而,现有的防水涂料不能长期有效地防雨水、抗冲刷。因此,经常看到装饰和涂刷整洁美观的建筑物经不住风雨冲刷和湿气浸蚀而色彩斑驳。主要是这些涂料中缺少化学性能稳定、不溶于水的无机物质,涂料性能与建筑物本体物理性能不相近。因而,其综合防水性能效果不佳,易老化。本专利技术要解决的技术问题是:为了克服上述涂料防水效果不佳、易老化等问题,提供了一种防水涂料,其能在长时间内保持较好的防水性能、防蒸汽性能。
技术实现思路
本专利技术解决其技术问题所采用的技术方案是:一种防水涂料,其特征在于由如下成分组成,其成分和重量百分比为:由如下成分组成:30~50%的苯乙烯-丙烯酸酯-丙烯酸共聚乳液,25~30%的石粉,0~5%的重钙,1~5%的防老剂,0~5%的消泡剂,0~5%的滑石粉,3~5%的气相二氧化硅,5~10%的聚乙烯醇,1~5%的水玻璃,10%的水。所述苯乙烯-丙烯酸酯-丙烯酸共聚物乳液中苯乙烯-丙烯酸酯-丙烯酸共聚物由苯乙烯、丙烯酸酯和丙烯酸按摩尔比10~30:10~30:1通过乳液聚合得到。本专利技术的有益效果是:该防水涂料防水,防蒸汽,附着力强,成膜硬度好;添加了防老剂和消泡剂,不易起泡,抗老化;石粉选用天然石料,具有相当的硬度,机械性能好,粘接性好,致密性好;聚乙烯醇具有防霉、增稠作用。具体实施方式现在结合实施例对本专利技术的具体实施方式做出进一步的详细说明,所属
的技术人员能够理解 ...
【技术保护点】
1.一种防水涂料,其特征在于:由如下成分组成,其成分和重量百分比为:苯乙烯‑丙烯酸酯‑丙烯酸共聚物乳液30~50%,石粉25~30%,重钙0~5%,防老剂1~5%,消泡剂0~5%,滑石粉0~5%,气相二氧化硅3~5%,聚乙烯醇5~10%,水玻璃1~5%,水10%。
【技术特征摘要】
1.一种防水涂料,其特征在于:由如下成分组成,其成分和重量百分比为:苯乙烯-丙烯酸酯-丙烯酸共聚物乳液30~50%,石粉25~30%,重钙0~5%,防老剂1~5%,消泡剂0~5%,滑石粉0~5%,气相二氧化硅3~5%,聚乙烯醇5~...