本发明专利技术提出一种双疏填料、用途及制备方法，由表面接枝具有双疏特性基团的空心微球组成，所述的双疏特性基团是通过空心微球在漂浮状态下与气化的含氟硅烷接枝反应得到。本发明专利技术通过高温活化处理、气流辅助分散、气相接触反应等手段制备得到表面双疏填料，在加热条件下提高了反应活性，气相状态增大了反应物接触面积，有利于获得表面双疏性能更佳的填料。

A double sparse filler, its application and preparation method

The invention provides a double sparse filler, application and preparation method, which is composed of a hollow microsphere with double sparse characteristic group grafted on the surface. The double sparse characteristic group is obtained by the grafting reaction of the hollow microsphere with gasified fluorosilane in the floating state. The surface double sparse filler is prepared by means of high temperature activation treatment, airflow assisted dispersion, gas phase contact reaction, etc. The reaction activity is improved under heating conditions, the gas phase state enlarges the contact area of the reactant, and the filler with better surface double sparse performance can be obtained.

【技术实现步骤摘要】
一种双疏填料、用途及制备方法
本专利技术涉及一种双疏填料、用途及制备方法，属于功能复合材料

技术介绍
窑炉、锅炉、管道等各种高温部件在工作过程中向外散发大量热量，一方面使设备本身能耗增加，另一方面也使周围环境温度升高影响其他设备正常工作或对操作人员造成损伤。隔热涂层因其耐温性高、隔热效果良好且施工工艺简便可作为各种高温部件外部隔热材料使用，起到降低设备能耗同时避免高温对其他设备和操作人员造成损伤的作用。常规隔热涂层包括耐高温无机涂层和有机硅耐高温隔热涂层两大类，无机涂层耐温高、成本较低，有机隔热涂层易于成膜、便于通过改性以具备多种功能。目前隔热涂层技术研究主要集中于改进涂层隔热性能、附着性等方面，鲜有对涂层制备后表面特性的研究，而隔热涂层在实际使用过程中常接触湿度大、油污多的恶劣环境，对涂层的隔热效果极易造成影响，使隔热效果下降甚至失效，因此需要对隔热涂层表面特性进行改进以规避水、油等污染对涂层性能的影响。现有技术中一般是通过在涂料中添加具有疏水疏油功能的助剂、填料或是直接对涂层的基体材料进行改性使涂层具有双疏特性。中国专利CN103572604A公布了1种防水防油剂及其制本文档来自技高网...

【技术保护点】
1.一种双疏填料，其特征在于：由表面接枝具有双疏特性基团的空心微球组成，所述的双疏特性基团是通过空心微球在漂浮状态下与气化的含氟硅烷接枝反应得到。

【技术特征摘要】
1.一种双疏填料，其特征在于：由表面接枝具有双疏特性基团的空心微球组成，所述的双疏特性基团是通过空心微球在漂浮状态下与气化的含氟硅烷接枝反应得到。2.根据权利要求1所述的一种双疏填料，其特征在于：所述的空心微珠与含氟硅烷质量比≤100：8。3.根据权利要求1所述的一种双疏填料，其特征在于：所述的空心微珠与含氟硅烷质量比为100：(10～15)。4.根据权利要求1所述的一种双疏填料，其特征在于：所述的空心微珠进行高温活化处理，高温活化处理工艺优选300℃～400℃下高温处理4～5h。5.一种权利要求1～4所述的双疏填料用于隔热涂料中。6.一种...