The invention relates to the technical field of hardening film, in particular to a hardening coating solution with high hardness and low reflectivity and a hardening film. In order to solve the problem of high reflectivity of hardening layer of existing hardening film, the invention provides a hardening coating solution with high hardness and low reflectivity and a hardening film. The hardening coating solution contains 25%-40% decagonal acrylate prepolymer, 25%-45% hexagonal acrylic resin prepolymer, 15%-35% hexafluoroacrylate monomer, 2%-6% photoinitiator, 0.2%-0.5% assistant, and the solid content is controlled in 15%-35%. The hardening layer formed by the hardening coating solution solidified by the invention has high hardness and low reflectivity. The hardening layer of the hardening film provided by the invention has high hardness, high wear resistance and low reflectivity.
【技术实现步骤摘要】
一种具有高硬度和低反射率的硬化层的硬化涂布液及硬化膜
本专利技术涉及硬化膜
，具体而言，涉及一种具有高硬度和低反射率的硬化层的硬化涂布液及一种硬化膜。
技术介绍
在LCD光学保护膜的诸多性能中，液晶显示器的显示画面在被周围环境的光线如阳光或外界灯光照射时会产生镜面反射而产生映入的现象，显示屏应该显示的画面就会和由外界映入的光和景观等重叠，使得显示图像清晰性下降，影响显示画面的观赏效果。解决此现象的较好方法是对显示屏进行防反射处理或在屏幕外侧使用防反射膜。而减反射最主要利用的就是光干涉的原理来减少镜片表面多余的反射光，提高透光率。目前常见的方法有干法涂布工艺，也就是利用化学气相沉淀工艺，把不同金属或氧化物沉积在薄膜上。另一种方法是湿法工艺，就是利用不同折射率的膜层界面对相应波长的光产生干扰而防止光的反射，涂膜厚度应由光的波长决定。在此之前，已有专利公布说明制备的湿法减反射方案中，一般都要求先做一层硬化液涂层，再以比较精确的厚度管控一层低折射率涂层。这种方式需要用到两步工序，相对工艺复杂，而且硬度和耐磨性也因为上面低折射涂层的厚度有影响。
技术实现思路
为了解决现有...
【技术保护点】
1.一种具有高硬度和低反射率的硬化层的硬化涂布液，其特征在于，所述硬化涂布液包括丙烯酸酯预聚物，和丙烯酸酯单体。
【技术特征摘要】
1.一种具有高硬度和低反射率的硬化层的硬化涂布液，其特征在于，所述硬化涂布液包括丙烯酸酯预聚物，和丙烯酸酯单体。2.根据权利要求1所述的硬化涂布液，其特征在于，所述硬化涂布液固化后形成硬化层，所述硬化层的反射率≤4.9％。3.根据权利要求1或2所述的硬化涂布液，其特征在于，所述硬化涂布液包括：25％～40％的十官丙烯酸酯预聚物，25％～45％的六官丙烯酸树脂预聚物，15％～35％六氟丙烯酸酯单体，2％～6％的光引发剂，和0.2％～0.5％的助剂，所述的百分比为重量百分比。4.根据权利要求3所述的硬化涂布液，其特征在于，所述硬化涂布液的固含量为15～35％。5.根据权利要求1或2所述的硬化涂布液，其特征在于，所述丙烯酸酯预聚物选自官能团≤10的丙烯酸酯预聚物。6.根据权利要求1所述的硬化涂布液，其特征在于，所述丙烯酸酯预聚物包括十官...
【专利技术属性】
技术研发人员：张彦，汪诚，简伟任，缪锴，夏寅，薛永富，唐海江，李刚，
申请(专利权)人：宁波激智科技股份有限公司，
类型：发明
国别省市：浙江,33