The invention discloses a ground waterproof coating and its preparation method. The components are as follows: deionized water 20 30 phr, water-borne acrylic polyurethane copolymer 40 50 phr, kaolin 20 30 phr, thickener 2 3 phr, defoamer 1 2 phr. The preparation method comprises the following steps: (1) adding 20 30 kaolin and 40 50 waterborne acrylic polyurethane copolymers into 20 30 deionized water to disperse and form mixed liquid A; (2) adding 1 2 defoamer and 2 3 thickener in turn into mixed liquid A, and pumping mixed liquid A into a disperser with high shear force for 40 minutes to mix liquid B; (3) mixing liquid B has been carried out. Waterproof coating can be obtained by filtration. The invention can achieve good waterproof effect, simple operation process and beneficial effect of large-scale production.
【技术实现步骤摘要】
一种地面防水涂料及其制备方法
本专利技术属于涂料
，特别涉及一种地面防水涂料及其制备方法。
技术介绍
目前内墙面主要出现的问题，大多是pH值变化造成水泥在水化过程中出现问题，造成内墙漆出现起泡、开裂等现象。酸性物质与水泥中的氢氧化钙会发生中和反应，生成物体积松散、膨胀，遇水后极易水解粉化，从而影响质量。因此，如何提高涂料的相关抗性，延长使用寿命，为各生产厂家所不断研究。
技术实现思路
本专利技术针对现有技术中存在的技术问题，提供一种地面防水涂料及其制备方法，可达到防水效果好，同时操作工艺简单，可大规模生产的有益效果。为解决上述技术问题，本专利技术采用的技术方案是：一种地面防水涂料，组分按照重量份数如下：去离子水20-30份，水性丙烯酸聚氨酯共聚物40-50份，高岭土20-30份，增稠剂2-3份，消泡剂1-2份。作为优选，增稠剂采用羟乙基纤维素。作为优选，消泡剂采用改性硅聚二甲基硅氧烷。一种地面防水涂料的制备方法，包括以下步骤：(1)将20-30份高岭土及40-50份水性丙烯酸聚氨酯共聚物加到20-30份去离子水中，进行分散，形成混合液A；(2)将1-2份消泡剂、...
【技术保护点】
1.一种地面防水涂料，其特征在于，组分按照重量份数如下：去离子水20‑30份，水性丙烯酸聚氨酯共聚物40‑50份，高岭土20‑30份，增稠剂2‑3份，消泡剂1‑2份。
【技术特征摘要】
1.一种地面防水涂料，其特征在于，组分按照重量份数如下：去离子水20-30份，水性丙烯酸聚氨酯共聚物40-50份，高岭土20-30份，增稠剂2-3份，消泡剂1-2份。2.根据权利要求1所述的一种地面防水涂料，其特征在于，增稠剂采用羟乙基纤维素。3.根据权利要求1所述的一种地面防水涂料，其特征在于，消泡剂采用改性硅聚二甲基硅...
【专利技术属性】
技术研发人员：谢朋超，赵晓博，胡安·阿兰戈，
申请(专利权)人：天津通用科技有限公司，
类型：发明
国别省市：天津,12