The invention provides a preparation method of a phase change heat storage capsule for thermal regulation of power lithium battery, which belongs to the technical field of power battery. The mixtures of 20-35wt% lithium nitrate, 1.5-5wt% sodium nitrate, 2.5-10wt% potassium nitrate, 2-10wt% calcium nitrate, 5-15wt% sodium nitrite, 15-35wt% sodium chloride, 1-6wt% potassium carbonate and 1-8wt% potassium sulfate were ground into fine powders. After sieving with 120-purpose sieves, the fine powders of molten salt with uniform particle size were formed. Four grams of sieved powders of molten salt and 3 grams of total hydrogen polysiloxane (PHP) S) n-butyl ether solution (mass fraction 30%) was mixed evenly in a round bottom flask. 150 g n-dodecane was added and stirred for 10 minutes. Then it was left for 30 minutes. The invention has the advantages of changing temperature 50-55 C, low cost and the like.
【技术实现步骤摘要】
用于动力锂电池热调控的相变储热胶囊的制备方法
本专利技术属于动力电池
，涉及一种用于动力锂电池热调控的相变储热胶囊的制备方法。
技术介绍
近年来，国内外新能源电动汽车市场发展火热，其动力来源主要是锂电池。锂离子电池综合电化学性能优异、比能量密度高达250WhKg-1，且在不断改进提高，同时制造成本不断下降，具有巨大的发展前景。然而锂离子电池也有其短板，在其频繁充放电过程中容易产热升温，如果该热量及温度不能及时加以控制，将极容易导致热失控而引起电池短路起火甚至爆炸，如：特斯拉电动汽车最近几年的多起燃烧爆炸事故。而一般情况下，动力锂电池的工作温度范围为10～60℃，因此其热安全性越来越受到重视。这些事故的主要原因是锂电池在充放电使用过程中的热失控现象。要解决锂电池的热失控现象，一个可行的方法是及时将锂电池在使用过程中产生的热及时吸收或者消除，以便电池维持在一个安全的温度范围(不超过60℃)。相对于繁琐且效率不高的强制风冷技术和直接液体冷却技术，相变储能材料可以在恒定的温度或很小的温度范围内吸收大量热量而维持电池处于低温安全状态。因此采用相变储能材料解决锂电池的热...
【技术保护点】
1.一种用于动力锂电池热调控的相变储热胶囊的制备方法，其特征在于，将20～35wt％硝酸锂、1.5～5wt％硝酸钠、2.5～10wt％硝酸钾、2～10wt％硝酸钙、5～15wt％亚硝酸钠、15～35wt％氯化钠、1～6wt％碳酸钾、1～8wt％硫酸钾组成的混合盐研磨成细粉，用120目的筛子过筛后形成粒径均匀的熔盐细粉；将4克过筛后的熔盐细粉与3克全氢聚硅氮烷(PHPS)的正丁醚溶液放入圆底烧瓶混合均匀，其中，全氢聚硅氮烷(PHPS)的正丁醚溶液占整个混合液的质量分数的30％，将混合液超声分散30分钟使之完全混合均匀，装入辐照塑料袋中，仔细排除袋中的空气，使溶液厚度保持为约1...
【技术特征摘要】
1.一种用于动力锂电池热调控的相变储热胶囊的制备方法，其特征在于，将20～35wt％硝酸锂、1.5～5wt％硝酸钠、2.5～10wt％硝酸钾、2～10wt％硝酸钙、5～15wt％亚硝酸钠、15～35wt％氯化钠、1～6wt％碳酸钾、1～8wt％硫酸钾组成的混合盐研磨成细粉，用120目的筛子过筛后形成粒径均匀的熔盐细粉；将4克过筛后的熔盐细粉与3克全氢聚硅氮烷(PHPS)的正丁醚溶液放入圆底烧瓶混合均匀，其中，全氢聚硅氮烷(PHPS)的正丁醚溶液占整个混合液的质量分数的...