A method for pouring liquid plastics is characterized by the following steps: (1) mixing Dibutyl Phosphate with vacuum oil and stirring evenly, then mixing polyvinyl chloride resin with calcium stearate, and then mixing the two mixtures evenly for 20 hours; (2) preheating the liquid plastics centering fixture body to 130 When the mixture is put into the container, the container is heated in the glycerol tank at 160 The liquid plastics pouring method of the invention can make the liquid plastics of the liquid plastics centering fixture body free of bubbles. When the movable column is pressurized on the liquid plastic, the liquid plastic can transfer the force evenly to the thin-walled sleeve, so that the thin-walled sleeve can produce uniform radial elastic deformation.
【技术实现步骤摘要】
一种液性塑料浇注方法
本专利技术涉及一种轴承内圈滚道加工的液性塑料定心夹具，尤其是一种液性塑料定心夹具中的液性塑料浇注方法。
技术介绍
目前，用于轴承内圈滚道超精研加工的定心夹具有三种类形：辊棒式、无心式和液压定心式。除了液压定心式外常用的定心式夹具还有：弹簧筒夹定心夹具、波纹套定心夹具和液性介质弹性定心夹具等。而液性介质弹性定心夹具采用液性塑料为介质的弹性定心夹具一般用于气缸等零件，在轴承加工设备中还没使用。为了将液性塑料定心夹具用于轴承内圈滚道超精研加工，需要设计一种定位精度高、夹紧力适合的液性塑料定心夹具。而液性塑料定心夹具制作中的关键是液性塑料浇注。
技术实现思路
本专利技术是要提供一种液性塑料浇注方法，该方法能完成液性塑料定心夹具中的液性塑料浇注，并使浇注的液性塑料无气泡，传递力均匀，使得液性塑料定心夹具定位精度高、夹紧力适合、适用于轴承内圈滚道螺旋超精研加工。为实现上述目的，本专利技术的技术方案是：一种液性塑料浇注方法，包括以下步骤：1）先将磷苯二甲酸二丁脂与真空油混合并搅拌均匀，再将聚氯乙烯树脂与硬脂酸钙拌合，然后将这二种混合物均匀混合在一起，放置20小时；2）浇注前，将液性塑料定心夹具体预热到130°-150℃；3）浇注时，将混合物放入容器内，将容器放在甘油槽内加热，加热温度为160°-170℃，并不断搅拌，使混合物呈透明白色的拉丝，保温15-20分钟，使混合物中的气泡上浮，然后，将混合物浇入液性塑料定心夹具体内。浇注后，让混合物在液性塑料定心夹具体内缓慢冷却，以免形成气泡。本专利技术的有益效果是：采用本专利技术的液性塑料浇注方法，可以使液性塑...
【技术保护点】
1.一种液性塑料浇注方法，其特征在于，包括以下步骤：（1）先将磷苯二甲酸二丁脂与真空油混合并搅拌均匀，再将聚氯乙烯树脂与硬脂酸钙拌合，然后将这二种混合物均匀混合在一起，放置20 小时；（2）浇注前，将液性塑料定心夹具体预热到130° ‑150℃ ；（3）浇注时，将混合物放入容器内，将容器放在甘油槽内加热，加热温度为160°‑170℃，并不断搅拌，使混合物呈透明白色的拉丝，保温15‑20 分钟，使混合物中的气泡上浮，然后，将混合物浇入液性塑料定心夹具体内。
【技术特征摘要】
1.一种液性塑料浇注方法，其特征在于，包括以下步骤：（1）先将磷苯二甲酸二丁脂与真空油混合并搅拌均匀，再将聚氯乙烯树脂与硬脂酸钙拌合，然后将这二种混合物均匀混合在一起，放置20小时；（2）浇注前，将液性塑料定心夹具体预热到130°-150℃；（3）浇注时，将混合物放入容器...