The invention discloses a new low-cost copper-sodium-manganese alloy rod and its preparation method, which comprises the following steps: adding copper, sodium and manganese into the industrial furnace for smelting; gradually adding manganese ingots until the composition requirements are met, in which the mass percent content of copper is 0.1 2%, the mass percent content of sodium is 0.05 0.1%, and the rest is manganese; adding refining agent for stirring refining; The melt of the alloy was heated at 450 500 C, and the manganese bar was obtained by pressure extrusion. The alloy manganese bars prepared by the method can be drawn into different lengths, diameters and shapes according to the requirements. The mechanical properties and corrosion resistance of the alloy manganese bars are similar to those of brass bars, and the cost is greatly reduced.
【技术实现步骤摘要】
一种新型低成本铜钠锰合金棒及其制备方法
本专利技术涉及一种锰棒制备
，特别涉及一种新型低成本铜钠锰合金棒及其制备方法。
技术介绍
黄铜棒被广泛的应用于空调管、冰箱管、机油管、给水管道以及各种机械配套用料，但是铜的价格居高不下，导致黄铜棒的成本很高。使用一种价格较低的金属棒材代替黄铜棒，已成为行业内共同面对的难题。
技术实现思路
本专利技术的目的是提供一种新型低成本铜钠锰合金棒及其制备方法，该制备方法得到的合金锰棒可以根据需求拉成不同长度、直径、形状，其机械性能、抗腐蚀性能与黄铜棒相当，成本得到大幅度下降。本专利技术提供一种新型低成本铜钠锰合金棒及其制备方法，包含以下步骤：S1、将铜、钠和锰加入工业炉进行熔炼；S2、逐步加入锰锭，直到达到成分要求，其中铜的质量百分含量为0.1-2％，钠的质量百分含量为0.05-0.1％，其余为所述锰；S3、加入精炼剂，进行搅拌精炼；S4、将精炼完成的合金熔液进行保温，温度控制在450-500℃；S5、通过挤压、刨皮、拉丝，得到合金锰棒。该制备方法得到的铜钠锰合金锰棒，使用时，机械性能、抗腐蚀性能与黄铜棒相当，但是成本得到大幅度下降...
【技术保护点】
1.一种新型低成本铜钠锰合金棒及其制备方法，其特征在于，包含以下步骤：S1、将铜、钠和锰加入工业炉进行熔炼；S2、逐步加入锰锭，直到达到成分要求，其中铜的质量百分含量为0.1‑2％，钠的质量百分含量为0.05‑0.1％，其余为所述锰；S3、加入精炼剂，进行搅拌精炼；S4、将精炼完成的合金熔液进行保温，温度控制在450‑500℃；S5、通过挤压、刨皮、拉丝，得到合金锰棒。
【技术特征摘要】
1.一种新型低成本铜钠锰合金棒及其制备方法，其特征在于，包含以下步骤：S1、将铜、钠和锰加入工业炉进行熔炼；S2、逐步加入锰锭，直到达到成分要求，其中铜的质量百分含量为0.1-2％，钠的质量百分含量为0.05-0.1％，其余为所述锰；S3、加入精炼剂，进行搅拌精炼；S4、将精炼完成的合金熔液进行保温，温度控...