The present invention is a copper-based alloy with vivid golden color and high corrosion resistance. It is based on Cu Al Zn and adds rare earth elements. It has good imitation golden color, strong sweat resistance, low cost and wide application. It can be used to manufacture various imitation gold or gold ornaments and decorations, such as jewelry, clock and watchcase belts, lamps and lanterns, mirror frames, medals and awards. Cups, utensils, decoration signs, tourist supplies, art ornaments, etc.
【技术实现步骤摘要】
一种具有逼真的黄金色泽和高耐蚀能力的铜基合金本专利技术涉及一种具有高仿金色泽和较强耐蚀性能的铜基合金,可广泛用于制造具有黄金色泽的各种仿金或金色的饰件饰物和装璜用品,诸如首饰挂件、艺术摆件、钟表壳带、镜架镜框、奖章奖杯、餐具茶具、灯具饰品、仪表盘匣、装璜标牌、旅游用品等等。本专利技术属于铜基合金或珠宝合金。在装饰装璜等场合,人们常用一些铜基合金代替黄金及其合金制造具有高贵典雅的黄金色泽的各种饰件饰物。因为这些铜基合金可用于制造戒指托、项链等与珠宝配伍的仿金饰件,故也有人称其为珠宝铜基合金的。传统使用的仿金铜基合金或者色泽不匀,容易褪色;或是仿金色差较大,抗汗液侵蚀性能偏差,并且含有In等较昂贵金属,成本较高。如联邦德国专利DE3235832和DE3235833所提供的两种含Ni或含Sn仿金铜基合金,其色泽与纯金色泽的色差较大;其对10%盐水的耐蚀性能虽有所改善,但依然缺乏较好的对人体汗液的抗蚀性能;又由于含Ni、Sn等较昂贵的金属,制造成本高。本专利技术的目的就在于提供一种具有高仿金色泽,色度坐标逼近纯金或金合金,并且抗人工汗液腐蚀能力较强的成本低廉的金色耐蚀铜基合金。本专利技术通过以下配方得以完成:其重量百分比为5~12%Al,3~11%Zn,或再加入0.01~2%的周期表中的3d元素或其氧化物,0.01~2%的稀土元素,其余为铜以及冶炼过程中带入的少量杂质。本专利技术的实施例之一如下:其重量百分比为6~8%Al,7.5~10.5%3d元素,0.01~1.5%Cr,0.01~1%稀土元素,其余为铜以及少量杂质。采用色度坐标为x=0.4213,y=0.398 ...
【技术保护点】
1.一种用于制造仿金或金色饰件饰物和装璜用品的金色铜基合金,其特征在于重量百分比为5~12%Al,3~11%Zn,0.01~2%的元素周期表中的3d元素或其氧化物,0.01~2%的稀土元素,其余为铜以及少量杂质。
【技术特征摘要】
1.一种用于制造仿金或金色饰件饰物和装璜用品的金色铜基合金,其特征在于重量百分比为5~12%Al,3~11%Zn,0.01~2%的元素周期表中的3d元素或其氧化物,0.01~2%的稀土元素,其...
【专利技术属性】
技术研发人员:吕淑敏,
申请(专利权)人:青岛海大智汇科技管理咨询有限公司,
类型:发明
国别省市:山东,37