The invention discloses a preparation method of foam copper powder, which belongs to the field of foam copper. The steps are as follows: selecting suitable copper oxide particles and mixing them, and the copper oxide particles are more than 40 mesh; adding pore forming agent into the mixed copper oxide particles, pore forming agent is calcium carbonate, and pore forming agent occupies a ratio of 30%; and the above mixture is put into reduction sintering furnace for reduction combustion. The sintered copper is made of sintered copper, the porosity of the sintered copper is 50% 80%, the reduction sintering temperature is 800 degrees C, 1000 degrees C, the reducing gas is carbon monoxide, and the above sintered copper is ground by ball mill and screened by different screens, and the copper foams with different particle sizes are obtained. The mesh size of the foam copper powder is between 20 mesh and 200 mesh.
【技术实现步骤摘要】
一种泡沫铜粉的制备方法
本专利技术涉及泡沫金属材料领域。
技术介绍
泡沫铜是一种在铜基体中均匀分布着大量连通或不连通孔洞的新型多功能材料。泡沫铜的导电性和延展性好，且制备成本比泡沫镍低，导电性能更好，可将其用于制备电池负极（载体）材料、催化剂载体和电磁屏蔽材料。特别是泡沫铜用于电池作电极的基体材料，具有一些明显的优点。泡沫铜是一种新型功能材料其主要应用于以下领域：（1）电极材料。优良的导电性能使泡沫铜可被广泛应用于镍锌电池、双电层电容器等新型电池的电极骨架材料，目前泡沫铜已获得多家镍锌电池生产厂家试用，并投入批量使用，同时，泡沫铜有望作为双电层电容器电极集流体获得推广应用；另外，泡沫铜作为电解回收含铜废水的电极材料使用，也具有非常广阔的前景。（2）催化剂。在许多有机化学反应中，人们尝试直接利用具有大比表面积的泡沫铜替代冲孔铜板，作为化学反应催化剂；泡沫铜作为光催化空气净化载体，也获得了较为成功的应用。（3）导热材料。泡沫铜具有优良的导热性能，使其成为性能优异的阻燃材料，在国外许多先进的消防器材上获得应用，尤其是作为火焰隔离器材具有优异的效果；另外，人们利用泡沫铜优...
【技术保护点】
1.一种泡沫铜粉的制备方法，其特征在于，步骤如下：步骤一、选取合适的氧化铜颗粒，并进行混合；步骤二、向上述混合的氧化铜颗粒中加入造孔剂；步骤三、将上述的混合物放入还原烧结炉中进行还原烧结，制得烧结铜；步骤四；利用球磨机将上述的烧结铜球磨，并利用不同筛网进行过筛，制得不同粒径的泡沫铜粉。
【技术特征摘要】
1.一种泡沫铜粉的制备方法，其特征在于，步骤如下：步骤一、选取合适的氧化铜颗粒，并进行混合；步骤二、向上述混合的氧化铜颗粒中加入造孔剂；步骤三、将上述的混合物放入还原烧结炉中进行还原烧结，制得烧结铜；步骤四；利用球磨机将上述的烧结铜球磨，并利用不同筛网进行过筛，制得不同粒径的泡沫铜粉。2.根据权利要求1所述的泡沫铜粉的制备方法，其特征在于，所述的氧化铜颗粒为40目以上。3.根据权利要求1所述的泡沫铜粉的制备方法，其特征在于，所述的造孔剂为碳酸钙、碳酸镁、碳酸氢钠、碳化硅、碳黑、氮化锰、氮...
【专利技术属性】
技术研发人员：李婵娟，
申请(专利权)人：乐山创新智谷工业设计有限公司，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。