The invention provides an ABS resin composition for improving laser welding performance and a preparation method thereof. The ABS resin composition comprises the following components: ABS rubber powder 30 50, SAN resin 30 60, heat resistant agent 5 10, polymethyl methacrylate 3 10, near infrared laser absorbent 1 5, antioxidant 0.1 1, lubricant 0.5 1.5. The preparation method comprises the following steps: the raw material is premixed in a high-speed mixer for 3 to 10 minutes, and then the premixed material is extruded and granulated by a twin-screw extruder. The invention has the advantages that the prepared ABS resin can not only improve the laser energy absorption ability of ABS matrix material, but also have excellent toughness, heat resistance and high melt strength. The resin composition is very suitable for laser welding with PMMA.
【技术实现步骤摘要】
一种适合激光焊接ABS组合物及其制备方法
本专利技术涉及高分子材料加工
，具体涉及一种适合激光焊接ABS组合物及其制备方法。
技术介绍
激光焊接是利用高能量密度的激光束作为热源的一种高效精密焊接方法。与传统焊接相比，激光焊接具有加热范围窄，作用位置和区域精确可控，焊接速度快，对外界没有热影响、噪音和污染等优点。激光焊接技术已经成为未来焊接的新趋势。使用激光焊接的两种聚合物中一种聚合物制品对于近红外激光是透射的，另一种聚合物制品吸收激光能量发热，使聚合物熔融，在界面处产生焊接。利用激光焊接工艺对聚合物进行焊接时，通过调节激光强度、焊接速度、焊接时间来控制制件外观以及焊缝强度。对于普通的ABS组合物，由于其吸收激光能力较差，需要较高的激光强度与较长的焊接时间。不仅生产周期长，生产效率低，同时容易造成焊接不良。能量过高时造成材料烧焦，能量不足时焊接强度低。因此，对于一种适合激光焊接，具有更高的材料加工窗口的ABS材料的存在需求。因此，专利技术设计适合激光焊接ABS组合物具有重要的科学意义和商业价值。公开号为CN105440639B的专利技术专利中公开了一种激光焊接...
【技术保护点】
1.一种适合激光焊接ABS树脂组合物，其特征在于，所述ABS树脂组合物包含以下重量份的各组分：
【技术特征摘要】
1.一种适合激光焊接ABS树脂组合物，其特征在于，所述ABS树脂组合物包含以下重量份的各组分：2.根据权利要求1所述的适合激光焊接ABS树脂组合物，其特征在于，所述ABS橡胶粉的重均相对分子质量为100000-500000，橡胶含量为30％-60％。3.根据权利要求1所述的适合激光焊接ABS树脂组合物，其特征在于，所述SAN树脂的重均相对分子质量为100000-300000，在220℃、10kg条件下熔体流动速率为1-15g/10min。4.根据权利要求1所述的适合激光焊接ABS树脂组合物，其特征在于，所述耐热剂包括以下重量百分含量的各组分：5.根据权利要求1所述的适合激光焊接ABS树脂组合物，其特征在于，所述聚甲基丙烯酸甲酯在220℃、10kg条件下，熔体流动速率为10-35g/10min；所述聚甲基丙烯酸甲酯的透光率大于85％。6.根据权利要求1所述的适合激光焊接ABS树脂组合物，其特征在于，所述近红外激光吸收剂...
【专利技术属性】
技术研发人员：李佳敏，于云安，周霆，辛敏琦，
申请(专利权)人：上海锦湖日丽塑料有限公司，
类型：发明
国别省市：上海,31