The invention discloses a graphite/alumina/polypropylene composite and a preparation method thereof. The graphite/alumina/polypropylene composite comprises the following weight percentage components: modified graphite 10_50%, modified alumina 10_30%, polypropylene 30_70%. The preparation method comprises the following steps: 1) surface treatment of graphite to obtain modified graphite; 2) surface treatment of alumina to obtain modified alumina; 3) co-asymmetric extrusion and mixing of modified alumina, polypropylene and liquid paraffin obtained in step 1 and step 2 to obtain graphite/alumina/polypropylene composite by extrusion granulation. The graphite/alumina/polypropylene composite of the invention has excellent mechanical properties, thermal properties and thermal conductivity, and is expected to be used in lighting lamp shade, LED radiator and household appliances shell.
【技术实现步骤摘要】
一种石墨/氧化铝/聚丙烯复合物及其制备方法
本专利技术属于导热高分子材料领域，具体涉及一种石墨/氧化铝/聚丙烯复合物及其制备方法。
技术介绍
随着工业生产和科学技术的发展，传统的导热材料，如金属、陶瓷等虽具有良好的导热性能，但是由于材料本身存在的缺陷或成本等因素，不能满足应用要求。对于热传导领域使用的材料，除了要求其具有良好的热传导性能，对材料的力学性能、电性能、热稳定性甚至加工性能都有一定要求。高分子材料拥有良好的综合性能，具有易改性、可塑性强和良好的加工性能等优点，应用领域广阔。然而，高分子材料通常是热的不良导体，在室温下的热导率较小，难以满足应用要求。聚丙烯具有质轻、易加工、耐腐蚀、力学均衡性好、价格低廉等优点，因此使用范围广。但聚丙烯导热性能差，其热导率只有0.21W/(m·K)，在散热器件、电子电器等领域的应用受到严重制约。采用单一的填料填充，对于改善高分子材料的导热性能效果有限。而使用不同粒径、不同形状甚至不同种类的多元填料混杂填充，可以使其形成更大的堆砌度，产生更多的导热通路。多元填料填充的高分子材料，不同导热填料之间产生互补效果与协同效应，导热性能...
【技术保护点】
1.一种石墨/氧化铝/聚丙烯复合物，其特征在于，包括以下重量百分比的组分：改性石墨10‑50％，改性氧化铝10‑30％，聚丙烯30‑70％。
【技术特征摘要】
1.一种石墨/氧化铝/聚丙烯复合物，其特征在于，包括以下重量百分比的组分：改性石墨10-50％，改性氧化铝10-30％，聚丙烯30-70％。2.根据权利要求1所述的石墨/氧化铝/聚丙烯复合物，其特征在于，改性石墨的粒径为10-20μm，改性氧化铝的粒径为1-5μm。3.根据权利要求1所述的石墨/氧化铝/聚丙烯复合物，其特征在于，改性石墨由以下方法制备：将石墨、硅烷偶联剂和无水乙醇混合，烘干，得到改性石墨。4.根据权利要求1所述的石墨/氧化铝/聚丙烯复合物，其特征在于，改性氧化铝由以下方法制备：将氧化铝、硅烷偶联剂和无水乙醇混合，烘干，得到改性氧化铝。5.一种制备权利要求1-4中任一项所述的石墨/氧化铝/聚丙烯复合物的方法，其特征在于，包括以下步骤：1)石墨的表面处理：将石墨、硅烷偶联剂和无水乙醇混合，烘干，得到改性石墨；2)氧化铝的表面处理：将氧化铝、硅烷偶联剂和无水乙醇混合，烘干，得到改性氧化铝；3)将步...
【专利技术属性】
技术研发人员：杜遥雪，杜思莹，徐百平，
申请(专利权)人：五邑大学，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。