The invention discloses a polypropylene composition, which comprises the following components by weight: 40 99 copies of polypropylene resin and 0.2 5 copies of polyketone. The preparation method is to mix the above components and add them to a high mixer with rotational speed of 1000 to 2000 rpm for 1 to 3 minutes, then melt the mixture through a twin-screw extruder with temperature of 190 to 230 degrees Celsius in each region of the screw and obtain the mixture by vacuum granulation. The invention also discloses the application of the polyketone in improving the thermal oxidation aging resistance of polypropylene compositions. By adding polyketone to the polypropylene composition, the heat and oxygen aging resistance of the polypropylene composition can be obviously improved.
【技术实现步骤摘要】
一种抗长期热氧老化聚丙烯组合物及其制备方法
本专利技术属于高分子材料加工改性领域，具体涉及一种聚丙烯组合物及其制备方法。
技术介绍
聚丙烯与其它通用塑料相比，具有力学性能好、密度小、刚性好、强度高以及电绝缘性能好等优点，但由于PP含有不稳定的叔碳基团，易受到热和氧的攻击而发生性能的劣变，如黄变、表面龟裂与粉化、力学性能大幅度下降。因此，许多产品都对聚丙烯提出长期耐热氧老化要求。中国专利CN101065432A公开了一种提高树脂耐热性的组合物，在组合物中添加主抗氧剂和二次氧化剂，增加组合物的稳定性，从而使组合物达到长期耐热氧老化性。虽然抗氧剂的加入是提高材料抗热氧老化性能的最直接最有效的方法之一，但是提高抗氧剂含量也会造成其他问题，例如增加成本压力和氧化剂析出等问题。提高抗氧剂含量也没有解决溶剂造成的白斑问题。本研究意外的发现，在聚丙烯组合物中加入聚酮，可以明显提高聚丙烯组合物的抗热氧老化性能。
技术实现思路
本专利技术的目的是提供一种聚丙烯组合物。本专利技术的另一目的是提供上述聚丙烯组合物的制备方法。本专利技术是通过以下技术方案实现的：一种聚丙烯组合物，按重量份计，包...
【技术保护点】
1.一种聚丙烯组合物，其特征在于，按重量份计，包括以下组分：聚丙烯树脂 40‑99份；聚酮 0.2‑5份。
【技术特征摘要】
1.一种聚丙烯组合物，其特征在于，按重量份计，包括以下组分：聚丙烯树脂40-99份；聚酮0.2-5份。2.根据权利要求1所述一种聚丙烯组合物，其特征在于，所述聚酮为符合以下分子通式的一种或几种：其中X为含至少三个碳原子的不饱和烯烃通过不饱和键聚合得到的部分。3.根据权利要求2所述聚丙烯组合物，其特征在于，所述不饱和烯烃选自丙烯、丁烯、己烯、辛烯、癸烯、苯乙烯、α-甲基苯乙烯、环戊烯、降冰片烯、四环十二烯、三环癸烯、五环十五烯、五环十六烯、氯化乙烯、氟化乙烯，优选为丙烯。4.根据权利要求2所述聚丙烯组合物，其特征在于，分子通式中的n：m不高于0.5，优选为0.01-0.1；熔点为220-240℃。5.根据权利要求1所述一种聚丙烯组合物，其特征在于，所述聚丙烯树脂为共聚聚丙烯树脂或均聚聚丙烯树脂中的任意一种或两种混合。6.根据权利要求1所述一种聚丙烯组合物，其特征在于，还包括重量份为0-30份的弹性体，所述弹性体为聚烯烃类弹性体，选自乙烯-丙烯共聚物、乙烯-己烯共聚物、乙烯-丁烯共聚物...
【专利技术属性】
技术研发人员：苏娟霞，杨波，丁正亚，罗忠富，林洁龙，彭莉，雷亮，卢朝亮，李振华，
申请(专利权)人：金发科技股份有限公司，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。