The invention discloses an electroless plating solution for coating nickel on the surface of BN ceramic particles by chemical deposition. The plating solution consists of nickel sulfate 20-30g/L, hydrazine hydrate 20-50ml/L, complexing agent 0.2-1.5ml/L, palladium chloride 1-5mg/L, ammonium sulfate 1-10g/L, surfactant 0.2-1.5g/ml, aminoacetic acid 0.2-1g/l, sodium acetate 8-17g/l, polyethylene glycol 0.5-1.6g/l, and the rest are solvent water. The bath with hydrazine hydrate as reducing agent, ammonia as complexing agent and sodium dodecyl sulfonate as surfactant has simple composition, good stability and good dispersibility, and can completely coat uniform and compact nickel layer on the surface of BN particles.
【技术实现步骤摘要】
一种用于BN陶瓷颗粒表面化学沉积包覆镍的化学镀溶液
本专利技术涉及化学镀
，尤其涉及一种用于BN陶瓷颗粒表面化学沉积包覆镍用的镀液
技术介绍
氮化硼为类石墨结构，具有良好的可磨耗性和自润滑性能，近年来金属或者合金包覆BN复合粉末材料被广泛用于航空航天涡轮发动机许多部件的低、中、高温可磨耗封严涂层，目前大部分制备金属或者合金包覆BN复合粉末材料时，所用的是以亚磷酸盐和硼烷衍生物为还原剂，但是以亚磷酸盐和硼烷衍生物为还原剂时，所得到的复合粉末材料中的镍层中均含有一定量的单质元素P和B，经长期高温使用后，会在镀层中产生Ni3B和Ni3P等中间相，且B元素还易引起晶间强化，对金属陶瓷符合涂层的自润滑和可磨耗性有害。以水合肼为还原剂的化学镀体系中虽然可得到纯的金属镀镍层，但是目前体系使用的络合剂如地酒酸钾钠、EDTA、乙醇酸等都存在镀液不稳定，工艺上可操作性差，特别是工业上应用成本高。
技术实现思路
本专利技术的目的在于提出一种BN陶瓷颗粒表面镀镍用的镀液，通过对镀液组成的调整，使直接面向BN陶瓷材料颗粒表面能够获得一层均匀致密的镍层，并且镍层可以完全包覆BN陶瓷颗粒形成...
【技术保护点】
1.一种用于BN陶瓷颗粒表面化学沉积包覆镍的化学镀溶液，所述镀液组成为：硫酸镍,水合肼,络合剂,氯化钯,硫酸铵,表面活性剂，氨基乙酸、醋酸钠，聚乙二醇，溶剂水，其特征在于络合剂为氨水、表面活性剂为十二烷基磺酸钠。
【技术特征摘要】
1.一种用于BN陶瓷颗粒表面化学沉积包覆镍的化学镀溶液，所述镀液组成为：硫酸镍,水合肼,络合剂,氯化钯,硫酸铵,表面活性剂，氨基乙酸、醋酸钠，聚乙二醇，溶剂水，其特征在于络合剂为氨水、表面活性剂为十二烷基磺酸钠。2.根据权利要求1所述的一种用于陶瓷颗粒表面化学沉积包覆镍的化学镀溶液，其特征在于所述镀液的组成为：硫酸镍15～35g/L,水合肼20～50ml/L,氨水0.2～1.5ml/L,氯化钯1～5mg/L,硫酸铵1～10g/L,十二烷基磺酸钠0.2～1.5g/ml，氨基乙酸0.2～1g/l、醋酸钠8～17g/l，聚乙二醇0.5～1.6g/l，其余为溶剂水。3.根据权利要求1或2所述的一种用于BN陶瓷颗粒表面化学沉积包覆镍的化学镀溶液，其特征在于所述毒液的组成为：硫酸镍26.5g/L,水合肼35ml/L,氨水0.9ml/L,氯化钯2.5mg/L,硫酸铵4.1g/...