The invention discloses a bearing cutting fluid and a preparation method, which is made of raw materials with the following weight ratios: 22 35 parts of phosphate ester, 15 25 parts of n-eleven-carbon dicarboxylic acid, 35 45 parts of emulsified silicone oil, 100 120 parts of deionized water, 15 22 parts of sodium petroleum sulfonate, 12 25 parts of glycerol, 5 12 parts of triazole corrosion inhibitor, 25 parts of diethanolamine, 12 parts of isopropanolamine, and melamine. Sodium phosphate 30 38, polyethylene glycol 40 55, nano-expanded graphite 3 8. The invention has the characteristics of environmental protection, good lubrication effect, good cooling effect, good rust prevention effect and hard water resistance.
【技术实现步骤摘要】
一种轴承切削液及制备方法
本专利技术涉及机加工领域用的切削液，特别是一种轴承切削液及制备方法。技术背景在轴承加工制造中，需要对轴承的零部件进行切削加工，在切削加工时，需要切削液对工件进行润滑、冷却，切削液由多种超强功能助剂经科学复合配合而成，其能够减少刀具磨损，提高刀具耐用度，从而提高生产效率，改善工件表面粗糙度，保证工件加工精度，达到最佳经济效果。传统的油基切削液防锈性、稳定性、冷却性及环保等方面已明显滞后于现代切削加工技术的发展，开始向无公害或低公害的水基切削液发展。
技术实现思路
：本专利技术的目的在于，提供一种轴承切削液及制备方法。本专利技术具有环保、润滑效果好、冷却效果好、防锈效果好和耐硬水的特点。为解决上述技术问题，本专利技术采用以下技术方案实现：一种轴承切削液，按重组分计，它是以下述重量配比的原料制成：磷酸酯22-35份、正十一碳二元羧酸15-25份、乳化硅油35-45份、去离子水100-120份、石油磺酸钠15-22份、甘油12-25份、三氮唑类缓蚀剂5-12份、二乙醇胺25-32份、异丙醇胺12-25份、三聚磷酸钠30-38份、聚乙二醇40-55...
【技术保护点】
1. 一种轴承切削液，其特征在于，按重组分计，它是以下述重量配比的原料制成：磷酸酯 22‑35份、 正十一碳二元羧酸 15‑25份、乳化硅油 35‑45份、 去离子水 100‑120份、石油磺酸钠 15‑22份、 甘油 12‑25份、三氮唑类缓蚀剂 5‑12份、 二乙醇胺 25‑32份、异丙醇胺 12‑25份、 三聚磷酸钠 ...
【技术特征摘要】
1.一种轴承切削液，其特征在于，按重组分计，它是以下述重量配比的原料制成：磷酸酯22-35份、正十一碳二元羧酸15-25份、乳化硅油35-45份、去离子水100-120份、石油磺酸钠15-22份、甘油12-25份、三氮唑类缓蚀剂5-12份、二乙醇胺25-32份、异丙醇胺12-25份、三聚磷酸钠30-38份、聚乙二醇40-55份、纳米膨化石墨3-8份。2.根据权利要求1所述的轴承切削液，其特征在于，按重组分计，它是以下述重量配比的原料制成：磷酸酯24-32份、正十一碳二元羧酸16-22份、乳化硅油36-42份、去离子水105-115份、石油磺酸钠16-20份、甘油14-22份、三氮唑类缓蚀剂6-10份、二乙醇胺26-30份、异丙醇胺10-22份、三聚磷酸钠32...
【专利技术属性】
技术研发人员：岑显礼，
申请(专利权)人：贵州丰达轴承有限公司，
类型：发明
国别省市：贵州,52