The present invention provides a two-component graphene heavy-duty anticorrosive coating, including component A and component B, in which the total weight of component A is 100%, including the following components: graphene 0.2-2wt%; epoxy resin 10-30wt%; zinc powder 20-50wt%; dispersant 0.5-3wt%; anti-settling agent 0.5-4wt%; defoamer 0.2-1wt%; silane coupling agent 0.2-1wt%. 2 wt%; thickener 0.3-2 wt%; pigments and fillers 10 20 wt%; first solvent 10-20 wt%; in which the zinc powder is a mixture of spherical zinc powder and scale zinc powder; the total weight of the B component is 100%, including the following components: curing agent 50-75 wt%; curing accelerator 1-5 wt%; second solvent 20-50 wt%.
【技术实现步骤摘要】
双组份石墨烯重防腐涂料及其制备方法
本专利技术属于重防腐涂料
，尤其涉及一种双组份石墨烯重防腐涂料及其制备方法。
技术介绍
环氧富锌涂料是一种耐腐蚀性能优异的重防腐涂料，被广泛应用于工业防腐的各个领域。环氧富锌涂料的防腐机理主要是锌的电化学保护作用，一般的，富锌涂料在发挥阴极保护作用时，其干膜中必须含有大量的锌粉粒子，其量足以使锌粉之间及锌粉和底材之间达到点接触程度。但涂层中锌粉含量过高，易导致涂层多孔，附着力、柔韧性和抗冲击强度下降。另一方面，环氧富锌涂料由于锌粉与基料密度相差较大，非常容易沉降，给施工和性能带来很不利的影响。为了减少沉降，通常采用触变剂，如气相二氧化硅、有机膨润土等作为防沉剂。此类触变剂是通过增加涂料黏度来防沉的，随着时间推移，防沉效果下降，且涂料黏度较大，很难制备高固体分涂料。
技术实现思路
本专利技术的目的在于提供一种双组份石墨烯重防腐涂料及其制备方法，旨在解决锌粉制备重防腐涂料时，由于锌粉含量高导致环氧富锌涂料容易沉降、涂层湿附着力低的问题。本专利技术是这样实现的，一种双组份石墨烯重防腐涂料，包括A组分和B组分，其中，以所述A组分的总重...
【技术保护点】
1.一种双组份石墨烯重防腐涂料，其特征在于，包括A组分和B组分，其中，以所述A组分的总重量为100％计，包括如下重量百分含量的下述组分：
【技术特征摘要】
1.一种双组份石墨烯重防腐涂料，其特征在于，包括A组分和B组分，其中，以所述A组分的总重量为100％计，包括如下重量百分含量的下述组分：其中，所述锌粉为球状锌粉和鳞片锌粉的混合物；以所述B组分的总重量为100％计，包括如下重量百分含量的下述组分：固化剂50～75wt％；固化促进剂1～5wt％；第二溶剂20～50wt％。2.如权利要求1所述的双组份石墨烯重防腐涂料，其特征在于，以所述锌粉的总重量为100％计，所述鳞片锌粉的重量百分含量为0-80％，且不为0。3.如权利要求1所述的双组份石墨烯重防腐涂料，其特征在于，所述分散剂为羧酸盐高分子分散剂。4.如权利要求1-3任一项所述的双组份石墨烯重防腐涂料，其特征在于，所述石墨烯含有表面官能团的单层或多层石墨烯，且所述表面官能团为极性基团。5.如权利要求1-3任一项所述的双组份石墨烯重防腐涂料，其特征在于，所述硅烷偶联剂为环氧基硅烷偶联剂。6.如权利要求1-3任一项所述的双组份石墨烯重防腐涂料，其特征在于，所述固化剂为聚酰胺650、聚酰胺125、改性胺固化剂中的至少一种；和/或所述固化促进剂为3-二乙氨基丙胺、DMP-30中的一种。7.如权利要求1-3任一项所述的双组份石墨烯重防腐涂料，其特征在于，所述颜填料为滑石粉、硫酸钡、钛白粉、长石粉、复合磷酸锌、云母粉、三聚磷酸...
【专利技术属性】
技术研发人员：孙学栋，
申请(专利权)人：深圳市烯世传奇科技有限公司，
类型：发明
国别省市：广东,44