The invention discloses a rubber with good mechanical properties, which is characterized by: the rubber comprises the following components: 260 280 copies of natural rubber, 120 150 copies of silicone rubber, 60 80 copies of mica, 10 20 copies of butadiene, 12 16 copies of sodium dodecylbenzenesulfonate, 8 12 copies of nano-zinc oxide, 8 copies of initiator, 8 copies of tertiary dodecyl mercaptan, 3 copies of tertiary dodecyl mercaptan, 6 copies of Rheinsan, 8 copies of initiator. Triallyl isocyanurate 2_4, diethylene glycol diacrylate 1_3, trimethylolpropane trimethacrylate 1_3, potassium oleate 2_6. The rubber obtained by the invention reduces the situation of the gel, so that the rubber products will not appear molecular breakage during the use process, and the strength and mechanical properties of the rubber products can fully meet the requirements of use.
【技术实现步骤摘要】
一种机械性能好的橡胶
本专利技术涉及橡胶
，尤其是涉及一种机械性能好的橡胶。
技术介绍
在生产橡胶的聚合过程中，都会产生因橡胶分子支化增多及分子间的化学交联而生成的在橡胶良溶剂中的不溶解物，就是线性分子的支化的增加或者是线性分子间相互反应形成的立体网状的体形大分子，这就是在橡胶生产过程中经常容易出现的凝胶现象，加上由于凝胶原因在橡胶中形成的体形较大的分子，导致橡胶在硫化反应中难以形成结构均匀的分子；导致在橡胶在成型的过程中受到较大的压力的情况下，得到的橡胶产品的机械性能较差，因此，现在的橡胶产品在使用的过程中极容易出现分子链的断裂，使得橡胶产品在使用过程中容易产生裂痕，使得现在的橡胶产品的强度和机械性能完全无法满足使用的要求。
技术实现思路
针对现有技术中的上述问题，本专利技术提出了一种机械性能好的橡胶，本专利技术解决了现在的橡胶容易出现凝胶的情况、导致橡胶产品在使用过程中极容易出现分子断裂以及橡胶产品的强度和机械性能不能满足使用要求等技术问题。本专利技术的技术方案为：一种机械性能好的橡胶，所述橡胶包括如下组分，按质量份数计，天然橡胶260-280份，硅橡胶12...
【技术保护点】
1.一种机械性能好的橡胶，其特征在于：所述橡胶包括如下组分，按质量份数计，天然橡胶260‑280份，硅橡胶120‑150份，云母60‑80份，丁二烯10‑20份，十二烷基苯磺酸钠12‑16份，纳米氧化锌8‑12份，引发剂8‑10份，叔十二碳硫醇3‑6份，莱茵散6‑8份，异氰尿酸三烯丙酯2‑4份，二乙二醇二丙烯酸酯1‑3份，三羟甲基丙烷三甲基丙烯酸酯1‑3份，油酸钾2‑6份。
【技术特征摘要】
1.一种机械性能好的橡胶，其特征在于：所述橡胶包括如下组分，按质量份数计，天然橡胶260-280份，硅橡胶120-150份，云母60-80份，丁二烯10-20份，十二烷基苯磺酸钠12-16份，纳米氧化锌8-12份，引发剂8-10份，叔十二碳硫醇3-6份，莱茵散6-8份，异氰尿酸三烯丙酯2-4份，二乙二醇二丙烯酸酯1-3份，三羟甲基丙烷三甲基丙烯酸酯1-3份，油酸钾2-6份。2.如权利要求1所述的一种机械性能好的橡胶，其特征在于：所述橡胶包括如下组分，按质量份数计，天然橡...
【专利技术属性】
技术研发人员：徐振东，
申请(专利权)人：四川振东精科汽车总成系统有限公司，
类型：发明
国别省市：四川,51