The invention provides an environmental protection foaming agent and a preparation method thereof. The foaming agent mainly comprises the following components: magnesium carbonate, sodium polyacrylate, sodium bicarbonate, diatomite, calcite, ultrafine aluminium powder, silicon carbide, carbonate, dichlorodifluoromethane, sodium bicarbonate, stabilizer and water. The preparation method of the environmental friendly foaming agent includes the following steps: 1. mixing magnesium carbonate, sodium polyacrylate, sodium bicarbonate, diatomite and calcite, crushing them into powder by a crusher, mixing the mixture evenly in the solvent to obtain solution A; 2. crushing the ultrafine aluminium powder, silicon carbide, carbonate, dichloromethane, sodium bicarbonate and stabilizer into powder by a crusher and pouring them into the powder. Mixing in water, reacting at 30
【技术实现步骤摘要】
一种环保发泡剂及其制备方法
本专利技术涉及材料工程领域，尤其涉及一种环保发泡剂及其制备方法。
技术介绍
发泡剂是指所有其水溶液能在引入空气的情况下大量产生泡沫的表面活性剂或表面活性物质。发泡剂具有较高的表面活性，能有效降低液体的表面张力，并在液膜表面双电子层排列而包围空气，形成气泡，再由气泡组成泡沫。目前，发泡剂被越来越广泛地使用。但是现有发泡物质也存在降解时间长、回收难的缺陷，会对环境造成较大污染。本专利技术主要提出一种制备过程简单，可大大降低对环境污染的环保发泡剂。
技术实现思路
本专利技术的目的是为了解决现有技术中存在的缺点，而提出的一种环保发泡剂及其制备方法。为了实现上述目的，本专利技术采用了如下技术方案：一种环保发泡剂，由以下组分原材料组成：碳酸镁20-36份、聚丙烯酸钠10-15份、碳酸氢钠15-23份、硅藻土20-45份、方解石4-8份、超细铝粉1-3份、碳化硅3-5份、碳酸盐1-3份、二氯二氟甲烷2-6份、碳酸氢钠0.5-1份、稳定剂5-10份、水50-80份。优选地，所述稳定剂包括有机锡、亚硫酸盐、钙皂、稀土均量混合而成。优选地，所述的碳酸盐为碳酸镁...
【技术保护点】
1.一种环保发泡剂，其特征在于，由以下组分原材料组成：碳酸镁20‑36份、聚丙烯酸钠10‑15份、碳酸氢钠15‑23份、硅藻土20‑45份、方解石4‑8份、超细铝粉1‑3份、碳化硅3‑5份、碳酸盐1‑3份、二氯二氟甲烷2‑6份、碳酸氢钠0.5‑1份、稳定剂5‑10份、水50‑80份。
【技术特征摘要】
1.一种环保发泡剂，其特征在于，由以下组分原材料组成：碳酸镁20-36份、聚丙烯酸钠10-15份、碳酸氢钠15-23份、硅藻土20-45份、方解石4-8份、超细铝粉1-3份、碳化硅3-5份、碳酸盐1-3份、二氯二氟甲烷2-6份、碳酸氢钠0.5-1份、稳定剂5-10份、水50-80份。2.根据权利要求1所述的一种环保发泡剂，其特征在于，所述稳定剂包括有机锡、亚硫酸盐、钙皂、稀土均量混合而成。3.根据权利要求1所述的一种环保发泡剂，其特征在于，所述的碳酸盐为碳酸镁。4.一种环保发泡剂的制备方法，其特征在于，包括以下步骤：S1、按标准将各组分称量，分开放置；S2、...
【专利技术属性】
技术研发人员：高宗旺，胡建明，
申请(专利权)人：瀚寅苏州新材料科技有限公司，
类型：发明
国别省市：江苏,32