一种能发荧光的PLA基体用于3D打印的复合材料制备制造技术

本发明专利技术公开了一种采用在3D打印PLA（聚乳酸）材料基体中，复合强化一种会发荧光的聚乳酸(PLA)和掺钐铝酸镁荧光粉(MgAl2O4:Sm3+)，制备出3D打印应用的生物塑料复合丝材。通过3‑氨基丙基三乙氧基硅烷对银光粉进行改性，从而增强了PLA与荧光粉的相容性，从而使得在PLA材料中引入荧光物质得以实现，并应用于3D打印技术领域，拓展了3D打印的应用范围和艺术审美等方面的广泛要求。

Preparation of a Fluorescent PLA Matrix Composite for 3D Printing

The invention discloses a bioplastic composite wire for 3D printing application, in which a fluorescent polylactic acid (PLA) and a Samarium-Doped magnesium aluminate phosphor (MgAl2O4:Sm3+) are combined and strengthened in a 3D printing PLA material matrix. Silver gloss powder was modified by 3_aminopropyl triethoxysilane, which enhanced the compatibility between PLA and phosphor, thus enabling the introduction of fluorescent materials into PLA materials to be realized, and applied in the field of 3D printing technology, expanding the application scope of 3D printing and artistic aesthetic requirements.

【技术实现步骤摘要】
一种能发荧光的PLA基体用于3D打印的复合材料制备
本专利技术涉及一种荧光3D打印材料的制备方法，更具体而言涉及一种发荧光的3D打印材料，利用该材料打印出来的样本模型刻广泛运用于美学附加值功能产品，提高产品的色彩、艺术和视觉表现力等效果。
技术介绍
近年来，由于对减少环境污染的需求增加，可降解和可再生塑料受到了广泛的关注。聚乳酸(PLA)是一种由玉米和甘蔗等可再生资源生产的生物塑料，已被证明是一种可行的解决方案。然而，聚乳酸并不像石油基聚合物那样无处不在，包括聚乙烯(PE)、聚丙烯(PP)、聚苯乙烯(PS)等，主要是由于经济原因和其较差的力学性能。因此，增强聚乳酸和提高聚乳酸的性能是聚乳酸研究的热点。因此，不同类型的填料被同时利用，包括纤维素、碳(纤维、纳米管等)以及碳酸钙(CaCO3)等无机填料。聚乳酸的制备采用了多种工艺。值得注意的是，3D打印最近获得了极大的业界关注，因为它为制造复杂形状的产品提供了更高的潜力，而这是传统的聚合物加工路线无法实现的，这些路线严重依赖模具，如压缩成型和注塑成型。3D打印机不仅可以在有限的空间内操作，只产生少量的加工废料，而且可以让打印出来的物体呈现本文档来自技高网...

【技术保护点】
1.本专利技术涉及一种PLA基体用于3D打印领域的荧光复合材料的制备方法，其特征在于通过在通用型3D打印PLA材料中复合改性钐铝酸镁荧光粉(MgAl2O4:Sm3+)，制备了用于3D打印的发光生物塑料复合丝。

【技术特征摘要】
1.本发明涉及一种PLA基体用于3D打印领域的荧光复合材料的制备方法，其特征在于通过在通用型3D打印PLA材料中复合改性钐铝酸镁荧光粉(MgAl2O4:Sm3+)，制备了用于3D打印的发光生物塑料复合丝。2.权利要求1所述的钐铝酸镁荧光粉(MgAl2O4:Sm3+)，其特征在于采用金属配合物分解法制备而成，因为这种制备方法出的荧光粉体粒度能够满足与PLA树脂的复合分散性要求。3.权利要求1中所述的荧光复合材料，其特征在于在4G5/2~6HJ(分别为5/2、7/2、9/2...

【专利技术属性】
技术研发人员：付远，姜江，程香平，
申请(专利权)人：江西省科学院应用物理研究所，
类型：发明
国别省市：江西,36