The invention provides a polypropylene composition, whose raw materials include: polypropylene graft, recycled nylon, chain extender and antioxidant, the average molecular weight of recycled nylon is 3000 10 000, and a preparation method of the polypropylene composition, including: step 1) mixing the polypropylene graft, recycled nylon, chain extender and antioxidant in proportion to obtain the mixture; The polypropylene composition is obtained by melt extrusion, cooling and granulation of the mixture. The polypropylene composition has the characteristics of low shrinkage, high toughness and high strength, and is especially suitable for use as a material for 3D printing.
【技术实现步骤摘要】
一种聚丙烯组合物及其制备方法和应用
本专利技术涉及石油化工领域，具体涉及一种聚丙烯组合物及其制备方法和应用。
技术介绍
3D打印是以计算机三维设计模型为蓝本，通过软件分层离散和数控成型系统，利用激光束、热熔喷嘴等方式将金属粉末、陶瓷粉末、塑料、细胞组织等特殊材料进行逐层堆积黏结，最终叠加成型，制造出实体产品的技术。3D打印凭借其独特的制造技术，可以生产前所未有的各类物品，并为企业减少成本、缩短工时以及去除复杂工艺，3D打印技术真正的优势在于其打印材料，可以很好地模仿塑料与金属材料的机械或者热能属性，然而这也是当前制约3D打印发展的一大技术原因。目前，用于熔融沉积成型打印工艺(FDM)的打印材料主要为丙烯腈-丁二烯-苯乙烯共聚物(ABS)和聚乳酸(PLA)等材料，但都存在不足之处，ABS为常见的工程塑料，采购容易，但加工易分解出有毒气体；PLA成本高、在55℃以上容易变形、力学性能差。但是，聚丙烯在3D打印领域由于受到打印工艺的限制，应用并不十分广泛，原因之一在于打印过程中由于自身结构规整，结晶速度快，收缩率高，使得牵引出的丝条直径不均匀，横截面不是圆形。这样卷材进...
【技术保护点】
1.一种聚丙烯组合物，其原料包括：聚丙烯接枝物、回收尼龙、扩链剂和抗氧剂，所述回收尼龙的数均分子量为3000‑10000。
【技术特征摘要】
1.一种聚丙烯组合物，其原料包括：聚丙烯接枝物、回收尼龙、扩链剂和抗氧剂，所述回收尼龙的数均分子量为3000-10000。2.根据权利要求1所述的聚丙烯组合物，其特征在于，以所述聚丙烯接枝物为100质量份数计，所述回收尼龙的含量为1-20质量份数，优选为5-15质量份数；所述扩链剂的含量为0.1-5质量份数，优选为0.1-1质量份数；所述抗氧剂的含量为0.1-3质量份数，优选为0.2-0.8质量份数。3.根据权利要求1或2所述的聚丙烯组合物，其特征在于，所述聚丙烯接枝物选自马来酸酐接枝聚丙烯、苯乙烯接枝聚丙烯以及马来酸酐和醋酸乙烯酯嵌段共聚物接枝聚丙烯中的至少一种，优选为马来酸酐接枝聚丙烯。4.根据权利要求1-3中任一项所述的聚丙烯组合物，其特征在于，所述回收尼龙选自尼龙破碎料和再生尼龙中的至少一种。5.根据权利要求1-4中任一项所述的聚丙烯组合物，其特征在于，扩链剂为含有环氧基团的低聚物，优选为苯乙烯-甲基丙烯酸缩水甘油酯共聚物、苯乙烯-丙烯酸缩水甘油酯、四氢邻苯二甲酸二缩水甘油酯和苯乙烯-丙烯腈-甲基丙烯酸缩水甘油酯共聚物中的至...
【专利技术属性】
技术研发人员：董穆，张师军，张琦，初立秋，邵静波，白弈青，徐毅辉，郭鹏，杨庆泉，邹浩，
申请(专利权)人：中国石油化工股份有限公司，中国石油化工股份有限公司北京化工研究院，
类型：发明
国别省市：北京,11