A macromolecule polymer modified magnesia expansive agent and its preparation method and application are as follows: (1) preparation of modifier: 1 20 mass fraction acetate polymer and 20 50 mass fraction organic solvent are stirred at 50 90 (?) C for 50 10 minutes until acetate polymer is completely dissolved to obtain modifier; (2) preparation of modified magnesia expansive agent: 30 90 (?) Modified magnesia expander was obtained by mixing 60 mass modifier with 100 mass magnesia expander and removing organic solvent. The modified magnesia expansive agent can adjust the hydration process of magnesia clinker, delay the hydration of magnesia, reduce the ineffective hydration in the plastic stage of concrete, increase the expansion of hardened concrete, and can be used for crack resistance and seepage prevention of concrete structure, and greatly improve the durability of concrete.
【技术实现步骤摘要】
一种高分子聚合物改性的氧化镁膨胀剂及其制备方法和应用
本专利技术属于建筑材料混凝土外加剂
，特别是涉及一种高分子聚合物改性的氧化镁膨胀剂及其制备方法和应用。
技术介绍
体积收缩是造成混凝土开裂、渗漏并影响混凝土耐久性能的主要原因之一。针对混凝土体积收缩问题，人们逐渐开发出各种类型的膨胀水泥和膨胀剂以补偿混凝土收缩，提高混凝土耐久性。膨胀剂是在膨胀水泥基础上发展而来的一种混凝土外加剂，掺入硅酸盐水泥中可拌制成膨胀混凝土。膨胀剂逐渐发展为混凝土行业中用量最大的外加剂之一，广泛应用于各类大型的混凝土施工工程，成为防止混凝土收缩开裂的有效产品。氧化镁膨胀剂是膨胀剂的一种，其膨胀特性可以调控设计，传统的方法是通过改变煅烧温度和保温时间来调控其膨胀性能。氧化镁膨胀剂是通过煅烧富镁矿物经粉磨而制得的。煅烧温度和保温时间对氧化镁的水化活性和膨胀性能有显著影响。高温煅烧的氧化镁，称死烧氧化镁，水化活性低，早期几乎不膨胀，开始产生膨胀所需时间长，可能需延迟至数年方产生膨胀。在此期间，原来趋于稳定的混凝土受到死烧氧化镁膨胀应力的影响而开裂破坏，造成安定性不良的问题。因此水泥熟料中...
【技术保护点】
1.一种高分子聚合物改性的氧化镁膨胀剂的制备方法，其特征在于制备步骤为：（1）改性剂的制备：将1‑30质量份的醋酸酯类聚合物和20‑50质量份的有机溶剂在50‑90℃搅拌10‑50分钟，直到醋酸酯类聚合物完全溶解，得到改性剂；（2）改性氧化镁膨胀剂的制备：将30‑60质量份的改性剂与100质量份的氧化镁膨胀剂混合搅拌，除去有机溶剂，得到改性氧化镁膨胀剂。
【技术特征摘要】
1.一种高分子聚合物改性的氧化镁膨胀剂的制备方法，其特征在于制备步骤为：（1）改性剂的制备：将1-30质量份的醋酸酯类聚合物和20-50质量份的有机溶剂在50-90℃搅拌10-50分钟，直到醋酸酯类聚合物完全溶解，得到改性剂；（2）改性氧化镁膨胀剂的制备：将30-60质量份的改性剂与100质量份的氧化镁膨胀剂混合搅拌，除去有机溶剂，得到改性氧化镁膨胀剂。2.根据权利要求1所述高分子聚合物改性的氧化镁膨胀剂的制备方法，其特征在于所述有机溶剂为甲醇、乙醇、三氯甲烷或丙酮。3.根据权利要求1所述高分子聚合物改性的氧化镁膨胀剂的制备方法，其特...
【专利技术属性】
技术研发人员：房健威，莫立武，项尚林，邓敏，
申请(专利权)人：南京工业大学，
类型：发明
国别省市：江苏,32