The invention provides a preparation method and electrocatalytic application of nitrogen doped CoMoO4 nanopowders with nanospherical structure. Firstly, cobalt-molybdenum pre-reaction liquid was disposed, heated in the reactor, cooled naturally for a period of time and centrifugally washed to obtain CoMoO4 nanopowders. Then, CoMoO4 nanopowders were doped with nitrogen, calcined at high temperature in ammonia atmosphere, and then cooled to room temperature to collect nanospherical nitrogen-doped CoMoO4 nanopowders. Nitrogen-doped CoMoO4 nanopowders with nanospherical structure have good electrocatalytic properties. The overpotential is as low as 0.280 V (relative to standard hydrogen electrode) and the Tafel slope is as low as 44 mV/dec.
【技术实现步骤摘要】
一种氮掺杂CoMoO4纳米球的制备方法及电催化应用
本专利技术涉及无机纳米球体的制备应用领域，具体涉及一种基于传统水热法制备氮掺杂CoMoO4纳米球的方法及电催化应用。
技术介绍
随着化石能源的不断消耗，其引发的环境问题及其有限性是世界持续发展的巨大障碍，对能源危机和污染问题的日益关注促使人们必须探索清洁、无污染的替代能源。近年来，氢能源由于能量密度高、可循环利用、清洁无污染等优点成为化石燃料的理想替代品，因此受到了全世界的广泛关注。电解水作为理想的产氢手段因工艺简单、安全、可控成为了目前研究的焦点。值得注意的是，电催化分解水过程中的阳极析氧反应由于涉及复杂的四电子过程具有缓慢的动力学特征，作为电解水的决速环节极大阻碍了其工业化生产。合适的催化剂能够降低反应的活化能，从而推动反应进行。目前最有效的催化剂是贵金属Pt、Ru及其氧化物，但贵金属的高成本和稀缺性严重限制了它们的大规模应用。因此，探索开发低成本、无毒、高效的电催化剂是当今时代发展面临的关键问题之一。纳米技术作为一种新兴科学技术，其潜在的重要性毋庸置疑，其独特的结构尺寸赋予了纳米粉体材料特别的物理化学性质，...
【技术保护点】
1.一种氮掺杂CoMoO4纳米球的制备方法，其特征在于，包括以下步骤（1）将钼源和钴源试剂加入有机溶剂中得到预反应液，加热一定时间后自然冷却，洗涤收集、真空干燥得到CoMoO4纳米粉体；（2）对CoMoO4纳米粉体进行氮掺杂，将CoMoO4纳米粉体置于氨气氛围下，煅烧一定时间，自然冷却，收集得到黑色纳米球状结构氮掺杂CoMoO4纳米粉体。
【技术特征摘要】
1.一种氮掺杂CoMoO4纳米球的制备方法，其特征在于，包括以下步骤（1）将钼源和钴源试剂加入有机溶剂中得到预反应液，加热一定时间后自然冷却，洗涤收集、真空干燥得到CoMoO4纳米粉体；（2）对CoMoO4纳米粉体进行氮掺杂，将CoMoO4纳米粉体置于氨气氛围下，煅烧一定时间，自然冷却，收集得到黑色纳米球状结构氮掺杂CoMoO4纳米粉体。2.根据权力要求书1所述一种氮掺杂CoMoO4纳米球的制备方法，其特征在于，所述步骤（1）中钼源为钼酸铵、三氧化钼、五氯化钼、四硫代钼酸铵、乙酰丙酮钼、钼酸钠中的一种或几种；浓度为1mmol/L~20mmol/L。3.根据权力要求书1所述一种氮掺杂CoMoO4纳米球的制备方法，其特征在于，所述步骤（1）中钴源为三氧化二钴、四氧化三钴、硫酸钴、九水合硝酸钴、醋酸钴、氯化钴中的...
【专利技术属性】
技术研发人员：孙旭，马晓晶，高令峰，郭成英，魏琴，
申请(专利权)人：济南大学，
类型：发明
国别省市：山东,37