The invention discloses a preparation method of coated anode plate, which includes: (1) selecting titanium plate as raw material and processing steps; (2) preparing steps of iridium-tantalum coating solution; (3) steps of pretreatment of titanium plate; (4) steps of roughness treatment; (5) steps of heat treatment; (6) covering iridium-tantalum liquid prepared repeatedly on the surface of substrate after heat treatment, and after each coating step. After sintering and cooling, they are coated next time; (7) cooling steps. The invention has excellent resistance to erosion of large amount of gas, impact of high current density, good adhesion with the matrix, and prolongs the service life of the electrode.
【技术实现步骤摘要】
涂层阳极板的制备方法
本专利技术涉及一种涂层阳极板的制备方法。
技术介绍
以金属钛或者其他阀型金属为基材，涂覆贵金属溶液为涂层的电极，在多种电化学领域诸如电解、电镀、有机电合成等行业大量被应用是众所周知的。而随着电化学工业的发展，在电子工业的电解铜箔领域，阳极电流密度明显加大。电极在使用过程中，会产生大量的气体，这种激烈的析气反应对于涂层的寿命产生了不良的影响，主要原因是这些气体在从龟裂纹中析出时，在涂层表面的形成的气泡的猛烈冲刷的机械作用，尤其是在电流密度较高的环境中，这种强烈的析气反应可能会导致原本就存在大量龟裂的涂层更容易出现剥落等现象，从而降低了阳极的寿命。
技术实现思路
本专利技术为了解决目前电极表面图层易剥落、寿命短的问题，为此提供了一种涂层阳极板的制备方法，包括以下步骤：(1)选用钛板为原料，并根据要求对原料剪切、拉网、冲孔加工成基体；(2)用氯铱酸、五氯化钽、四氯化锡、盐酸和正丁醇制备铱钽涂液的步骤；(3)对钛板进行前处理，依次为水洗→除油剂除油→酸洗→水洗→醇洗；(4)采用刻蚀和/或喷砂工艺处理将基体粗糙度处理至Rz≥30；(5)热处理的步骤；(6)...
【技术保护点】
1.一种涂层阳极板的制备方法，其特征在于，包括以下步骤：(1)选用钛板为原料，并根据要求对原料剪切、拉网、冲孔加工成基体；(2)用氯铱酸、五氯化钽、四氯化锡、盐酸和正丁醇制备铱钽涂液的步骤；(3)对钛板进行前处理，依次为水洗→除油剂除油→酸洗→水洗→醇洗；(4)采用刻蚀和/或喷砂工艺处理将基体粗糙度处理至Rz≥30；(5)热处理的步骤；(6)将步骤(2)制备好的铱钽涂液多次覆在步骤(5)热处理后的基体表面，在每次涂覆之后均经烧结冷却再涂覆下一次，且最后一次烧结时间最长；(7)冷却的步骤。
【技术特征摘要】
1.一种涂层阳极板的制备方法，其特征在于，包括以下步骤：(1)选用钛板为原料，并根据要求对原料剪切、拉网、冲孔加工成基体；(2)用氯铱酸、五氯化钽、四氯化锡、盐酸和正丁醇制备铱钽涂液的步骤；(3)对钛板进行前处理，依次为水洗→除油剂除油→酸洗→水洗→醇洗；(4)采用刻蚀和/或喷砂工艺处理将基体粗糙度处理至Rz≥30；(5)热处理的步骤；(6)将步骤(2)制备好的铱钽涂液多次覆在步骤(5)热处理后的基体表面，在每次涂覆之后均经烧结冷却再涂覆下一次，且最后一次烧结时间最长；(7)冷却的步骤。2.根据权利要求1所述的涂层阳极板的制备方法，其特征在于，步骤(2)制得的铱钽涂液中氯铱酸、五氯化钽、四氯化锡、盐酸和...
【专利技术属性】
技术研发人员：程亚云，
申请(专利权)人：江阴安诺电极有限公司，
类型：发明
国别省市：江苏,32