The invention discloses a high flexibility powder coating and its method, which is suitable for pipes. The powder coating is composed of 60 80 parts of epoxy resin, 10 20 parts of phenolic curing agent, 0.5 5 parts of toughening agent, 0.5 3 parts of flow aids, 0.1 1 part of antioxidant, 1 10 parts of pigments and 5 35 parts of fillers. The method comprises the following steps: 1) mixing raw materials according to the weight of raw materials; 2) Extruding and melting homogeneous materials into twin-screw extruder, the melting extrudate is cooled by direct pressing of cooling roller, the temperature of each temperature zone of extruder is 95 115 C; 3) crushing by crusher, then grinding by grading and sieving equipment to obtain the final powder coating; The invention provides a powder coating with high flexibility and non-cracking and a method.
【技术实现步骤摘要】
一种高柔韧性粉末涂料及其方法
本专利技术涉及管材涂料领域，尤其涉及一种高柔韧性粉末涂料及其方法。
技术介绍
相对于传统溶剂型涂料，粉末涂料具有无溶剂性、无环境污染、粉末回收和利用率高等特点。自从1970年代石油危机，粉末涂料便以其环保，绿色节能等特点，得到了迅速的发展，成为了一种重要的涂料新产品。粉末涂料一般由树脂，固化剂(热塑性粉末涂料中不含)，颜料，填料，助剂等成分。环氧粉末涂料是20世纪60年代开发的热固性的粉末涂料，由环氧树脂，固化剂，颜料，填料，助剂等组成。环氧树脂分子结构内有大量的羟基，使得与金属等基材的附着力优异。涂膜的硬度高，抗划伤性能优异。成膜分子结构中不含有酯基，耐腐蚀性能和耐化学性能突出，特别适合应用在防腐和防锈涂装方面。由于环氧粉末涂料出色的性能，目前被广泛应用到不同管径的输气，输油，输水管道内外壁的涂装上，同时在化工厂的物料输送管道，船舶管道，矿井支撑架，钢筋，脚手架等重防腐领域也得到了大量的应用。目前市场上常见的环氧粉末涂料产品，虽然能满足管道一般防腐的要求，但普遍存在的问题是厚涂时涂层的柔韧性不好，满足不了管道厂家沟槽后加工的需求，甚...
【技术保护点】
1.一种高柔韧性粉末涂料，适用于管材，其特征在于，所述粉末涂料为以下原料组分及重量份：
【技术特征摘要】
1.一种高柔韧性粉末涂料，适用于管材，其特征在于，所述粉末涂料为以下原料组分及重量份：所述环氧树脂的环氧当量是所述酚类固化剂的酚羟基当量的1.2-5.5倍。2.如权利要求1所述高柔韧性粉末涂料，其特征在于，所述环氧树脂的环氧当量为600-1100g/eq，软化点为90-110℃。3.如权利要求1所述高柔韧性粉末涂料，其特征在于，所述酚类固化剂的酚羟基当量为200-500g/eq，软化点为80-100℃。4.如权利要求1所述高柔韧性粉末涂料，其特征在于，所述增韧剂为聚乙烯醇缩丁醛。5.如权利要求1所述高柔韧性粉末涂料，其特征在于，所述抗...
【专利技术属性】
技术研发人员：蔡锋，黄建，毕宏江，王磊，
申请(专利权)人：上海邦中新材料有限公司，
类型：发明
国别省市：上海,31