本发明专利技术涉及印刷技术领域，公开了一种水性UV油墨,由以下重量百分比的原料组成：硅烷基改性丙烯酸树酯20‑30%；水性UV单体；助剂1‑3%；光引发剂3‑5%；去离子水加至100%。油墨气味小，刺激性小，力学性能良好，附着力优异，耐化学性好，固化后外表平滑光洁。使用中达到了性能和环保双方面的兼顾。本发明专利技术的水性油墨的适应多种印刷方式，可应用于食品、药品等包装的印刷。

A Waterborne UV Ink and Its Preparation Method

The invention relates to the printing technology field, and discloses a water-borne UV ink, which consists of raw materials with the following weight percentage: silicone modified acrylic resin 20 30%; water-borne UV monomer; additive 1 3%; photoinitiator 3 5%; deionized water 100%. Ink has small odor, little irritation, good mechanical properties, excellent adhesion, good chemical resistance and smooth appearance after curing. Both performance and environmental protection are taken into account in use. The water-based ink of the invention is suitable for various printing methods and can be applied to the printing of food, medicine and other packaging.

【技术实现步骤摘要】
一种水性UV油墨及其制备方法
本专利技术涉及印刷
，具体涉及一种水性UV油墨及其制备方法。
技术介绍
水性油墨(Water-basedink)简称为水墨，它主要由水溶性树脂、有机颜料、溶剂及相关助剂经复合研磨加工而成。水性油墨特别适用于烟、酒、食品、饮料、药品、儿童玩具等卫生条件要求严格的包装印刷产品。由于用水作溶解载体，水性油墨具有显著的环保安全特点：安全、无毒无害、不燃不爆，几乎无挥发性有机气体产生，是国家近年来大力发展的油墨品种。
技术实现思路
本专利技术所要解决的技术问题是提供一种水性UV油墨。本专利技术所要解决的技术问题通过以下技术方案予以实现：一种水性UV油墨，所述水性油墨由以下重量百分比的原料组成：硅烷基改性丙烯酸树酯20-30%；水性UV单体10-15%助剂1-3%；光引发剂3-5%；去离子水加至100%。进一步的，所述的水性UV单体包括乙氧化三羟甲基丙烷三丙烯酸酯、聚乙二醇单甲基丙烯酸酯、甲氧基聚乙二醇单丙烯酸酯中的任意一种。此类单体具有低VOC、宽光泽范围，较好的耐化学品性能。进一步的，所述的光引发剂为1-[4-(2-羟乙氧基)-亚苯基]-2-羟基-2′和/或2本文档来自技高网...

【技术保护点】
1.一种水性UV油墨，其特征在于，由以下重量百分比的原料组成：硅烷基改性丙烯酸树酯20‑30%；水性UV单体10‑15%助剂1‑3%；光引发剂3‑5%；去离子水加至100%。

【技术特征摘要】
1.一种水性UV油墨，其特征在于，由以下重量百分比的原料组成：硅烷基改性丙烯酸树酯20-30%；水性UV单体10-15%助剂1-3%；光引发剂3-5%；去离子水加至100%。2.根据权利要求1所述的水性UV油墨，其特征在于，所述的水性UV单体包括乙氧化三羟甲基丙烷三丙烯酸酯、聚乙二醇单甲基丙烯酸酯、甲氧基聚乙二醇单丙烯酸酯中的任意一种。3.根据权利要求1所述的水性UV油墨，其特征在于，所述的光引发剂为1-[4-(2-羟乙氧基)-亚苯基]-2-羟基-2′和/或...