The invention discloses a low-temperature flame-retardant PA66/PPO composite material, which is characterized by the following components according to weight percentage: PA6645-65%, PPO 10-15%, low-temperature cold-resistant agent 10-15%, compatibilizer 2-5%, flame retardant 8-12%, flame retardant synergist 5-6%, toughener 3-8%, antioxidant 0.2-0.6%, processing aids 0.3-0.8%. Further, the preparation method of the material is disclosed. The invention takes PA66/PPO as matrix resin, halogen and antimony as flame retardants, and improves the toughness of composite materials under low temperature conditions by introducing low temperature cold-resistant agent.
【技术实现步骤摘要】
一种耐低温阻燃PA66/PPO复合材料及其制备方法[
]本专利技术涉及一种高分子材料改性
，尤其涉及一种耐低温阻燃PA66/PPO复合材料及其制备方法。[
技术介绍
]聚酰胺66俗称尼龙66，分子链上含有重复酰胺基团的热塑性树脂。因其具有耐化学性和耐磨性能好，力学性能优异，自润滑性和韧性好等诸多优良性能，广泛应用于机械、汽车、仪器仪表等领域。同时在电子电器领域，PA66阻燃材料通常也作为电器产品外壳优选阻燃材料。聚苯醚(PPO)具有耐水性好，尺寸稳定性优异，阻燃效果好，离火自熄。因此，将PPO与PA66共混制备PA66/PPO复合材料能够大幅提高PA66材料的阻燃性能。但是阻燃PA66/PPO复合材料的韧性难以满足在低温条件下的使用要求。[
技术实现思路
]本专利技术的目的是针对现有技术的不足，提供一种耐低温阻燃PA66/PPO复合材料及其制备方法。本专利技术以PA66/PPO为基体树脂，以卤系和锑系为阻燃剂，通过引入低温耐寒剂改善复合材料在低温条件下的韧性。本专利技术的技术方案如下：一种耐低温阻燃PA66/PPO复合材料及其制备方法，其特征在于，由下列组分按重...
【技术保护点】
1.一种耐低温阻燃PA66/PPO复合材料，其特征在于，按重量百分比由以下组分组成：
【技术特征摘要】
1.一种耐低温阻燃PA66/PPO复合材料，其特征在于，按重量百分比由以下组分组成：2.根据权利要求1所述的一种耐低温阻燃PA66/PPO复合材料，其特征在于，所述PA66树脂的相对粘度为2.7～2.8dl/g。3.根据权利要求1所述的一种耐低温阻燃PA66/PPO复合材料，其特征在于，所述PPO树脂的特性粘度为0.3～0.5dl/g。4.根据权利要求1所述的一种耐低温阻燃PA66/PPO复合材料，其特征在于，所述低温耐寒剂为乙烯-甲基丙烯酸离子聚合物。5.根据权利要求1所述的一种耐低温阻燃PA66/PPO复合材料，其特征在于，所述相容剂为SBS接枝马来酸酐。6.根据权利要求1所述的一种耐低温阻燃PA66/PPO复合材料，其特征在于，所述阻燃剂为卤系阻燃剂，如十溴二苯乙烷或者溴代三嗪等，所述阻燃协效剂为三氧化二锑。7.根据权利要求1所述的一种耐低温阻燃PA66/PPO复合材料，其特征在于，所述增韧剂为乙烯与辛烯共聚物(POE)，优选马来酸酐接枝改性的乙烯与辛烯共聚物。8.根据权利要求1所述的一种耐低温阻燃PA66/PPO复合材料，其...