本发明专利技术涉及一种PA66‑AES复合材料，其组成按重量份由以下组分组成：PA66为60份‑70份；AES为20份‑30份；HDPE为5份‑10份；相容剂为0.1份‑0.3份；耐磨剂为4份‑6份；抗氧剂为0.1份‑0.5份；抗UV剂为0.1份‑0.3份；润滑剂为0.1份‑0.3份；色粉为0.1份‑0.5份。相容剂SEBS‑g‑MAH的加入，有利于PA66和AES的分散；与其它耐磨剂相比，硅酮母粒MB50‑007可以改善PA66‑AES的耐磨性，对其力学性能几乎没有影响；抗UV的加入改善了PA66‑AES材料的耐候性。

A PA66-AES Composite Material

The present invention relates to a PA66 AES composite material, which consists of 60 70 parts by weight, 20 30 parts by AES, 5 10 parts by HDPE, 0.1 0.3 parts by compatibility, 4 6 parts by wear resistance, 0.1 0.5 parts by antioxidant, 0.1 0.3 parts by UV resistance, 0.1 0.3 parts by lubricant, 0.1 0.5 parts by color powder. The addition of compatibilizer SEBS g MAH is beneficial to the dispersion of PA66 and AES. Compared with other wear-resistant agents, silicone masterbatch MB50 007 can improve the wear resistance of PA66 AES, and has little effect on its mechanical properties. The addition of UV resistance improves the weatherability of PA66 AES materials.

【技术实现步骤摘要】
一种PA66-AES复合材料
本专利技术属于新材料
，特别是指一种PA66-AES复合材料。
技术介绍
聚酰胺(PA66)是一种性能优良的工程塑料，但存在吸水性高，尺寸稳定性较差、低温和干燥环境中冲击强度差等缺陷，从而限制了它在某些领域的应用。丙烯晴-三元乙丙橡胶-苯乙烯(AES)具有较高的冲击强度、良好的加工稳定性，但其本身耐候性、耐化学腐蚀性等性能不佳，这些均限制了AES树脂的进一步应用。鉴于此原因，将PA66与AES共混，以使得PA66与AES的性能互补，是本领域一直致力于研究的课题。
技术实现思路
本专利技术的目的是提供一种PA66-AES复合材料，以提高复合材料的性能。本专利技术是通过以下技术方案实现的：一种PA66-AES复合材料，其组成按重量份由以下组分组成：所述AES中三元乙丙橡胶的重量百分比含量为60％。所述相容剂为SEBS-g-MAH。所述耐磨剂为硅酮母粒MB50-007。所述抗氧剂为(2，4-二叔丁基)亚磷酸苯酯、四[β-(3，5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯或1，3，5-三甲基-2，4，6-(3，5-二叔丁基-4-羟基苯甲基)苯中的一种或几种的混本文档来自技高网...

【技术保护点】
1.一种PA66‑AES复合材料，其特征在于，其组成按重量份由以下组分组成：

【技术特征摘要】
1.一种PA66-AES复合材料，其特征在于，其组成按重量份由以下组分组成：2.根据权利要求1所述的PA66-AES复合材料，其特征在于，所述AES中三元乙丙橡胶的重量百分比含量为60％。3.根据权利要求1所述的PA66-AES复合材料，其特征在于，所述相容剂为SEBS-g-MAH。4.根据权利要求1所述的PA66-AES复合材料，其特征在于，所述耐磨剂为硅酮母粒MB50-007。5.根据权利要求1所述的PA66-AES复合材料，其特征在于，所述抗氧剂为(2，4-二叔丁基)亚磷酸苯酯、四[...