The invention relates to the technical field of polyurethane adhesives, in particular to a fast curing low temperature flexible polyurethane adhesives, a preparation method and a use method thereof. The adhesives of the invention include raw materials with the following weight percentage contents: polyether polyol 55 65%; isocyanate 25 30%; composite plasticizer 8 15%; antifungal agent 1 5%; catalyst 0.5 2%. The composite plasticizer is three or four of medium-chain chlorinated paraffin C14 C17, long-chain chlorinated paraffin C18 C28, chloropalm oleate formate and 2,2,4 trimethyl 1,3 pentanediol diisobutyrate. The binder improves the curing speed at low temperature, facilitates construction, improves construction efficiency, maintains relatively good flexibility in long-term low temperature environment, has good anti-mildew performance, and is convenient for daily sports use.
【技术实现步骤摘要】
快速固化低温柔韧性聚氨酯粘合剂及其制备方法和使用方法
本专利技术涉及聚氨酯粘合剂
，具体涉及一种快速固化低温柔韧性聚氨酯粘合剂及其制备方法和使用方法。
技术介绍
聚氨酯产品属于国家重点发展的新材料产品，聚氨酯铺装粘合剂被广泛的应用到田径场地的各个领域。2016年10月25日，中共中央、国务院印发了《“健康中国2030”规划纲要》，提到2030年健康服务业总规模将达16万亿元、到2030年经常参加体育锻炼人数达到5.3亿人、确保学生校内每天体育活动时间不少于1小时。国家标准方面，2018年GB36246-2018《中小学合成材料面层运动场地》正式发布实施，并且上升到强制标准，聚氨酯铺装粘合剂的发展即将步入一个新的阶段。我国幅员辽阔，北起漠河以北，南到南沙群岛南端，南北相距约5500公里，气候温度范围更是由热带到寒温带，对于多样化的气候环境，对于聚氨酯粘合剂的要求更是多种多样、因地制宜，尤其在较为寒冷的北方，环境温度和相对湿度较低，要求聚氨酯粘合剂的能在低温低湿下仍达到一定的固化速度，且在相当长时期的低温环境中保持相对良好的柔韧性能，方便日常的运动使用。目前国内...
【技术保护点】
1.一种快速固化低温柔韧性聚氨酯粘合剂，其特征在于：包括以下重量百分含量的原料：
【技术特征摘要】
1.一种快速固化低温柔韧性聚氨酯粘合剂，其特征在于：包括以下重量百分含量的原料：所述复合增塑剂为C14-C17的中链氯化石蜡、C18-C28的长链氯化石蜡、氯代棕榈油甲酸酯和2,2,4-三甲基-1,3-戊二醇双异丁酸酯中的三种或四种；所述催化剂为有机金属催化剂和有机胺类催化剂的混合物，混合质量比为3:1。2.根据权利要求1所述的快速固化低温柔韧性聚氨酯粘合剂，其特征在于：聚醚多元醇为以甘油为起始剂、环氧丙烷开环、环氧乙烷封端、官能度为2-3、数均分子量为2000-4000的聚醚多元醇。3.根据权利要求1所述的快速固化低温柔韧性聚氨酯粘合剂，其特征在于：异氰酸酯为MDI-50、纯MDI、聚合MDI、TDI中的一种或多种。4.根据权利要求1所述的快速固化低温柔韧性聚氨酯粘合剂，其特征在于：抗霉菌剂为纳米银类抗菌剂。5...
【专利技术属性】
技术研发人员：梁玲，刘浩特，李立强，申建洲，
申请(专利权)人：山东一诺威体育产业有限公司，
类型：发明
国别省市：山东,37