The invention discloses a surface non-bonding matte soft TPU, which comprises the following weight parts: thermoplastic polyurethane elastomer TPU: 60 copies; extinction agent: 5 copies; compatibilizer: 5 copies 10 copies; anti-sticking agent: 0.5 copies; 1 copies; in this invention, as a key technology, the use of anti-sticking agent successfully solves the matte soft TPU. At the same time, it avoids the migration and precipitation of EBS and polyethylene wax caused by the surface sticking of soft TPU products, such as EBS and polyethylene wax, which are usually used to solve the problem of frosting.
【技术实现步骤摘要】
一种表面不粘结哑光型软质TPU及其制备方法
本专利技术涉及高分子材料，更具体的说是涉及一种表面不粘结哑光型软质TPU。
技术介绍
TPU在现有技术中主要分为硬质和软质，软质的TPU硬度范围在35A至70A之间，其由软段相和硬度相构成，因两相热力学不相容而产生微相分离，下游可用于挤出、注塑、吹塑、流延。哑光型软质TPU因其特有的触感和表面效果使得在很多领域得到应用，如止滑鞋底，玩具，宠物用品等，但哑光型软质TPU的开发技术难点主要分两方面：一是相容性和制品表面发粘。哑光型软质TPU制品表面发粘限制了很多下游应用，现有的解决方案多为在产品生产过程中添加大量的常规外滑助剂如EBS、聚乙烯蜡等来降低表面粘结性，但缺点是制品表面会随着时间推移而导致EBS、聚乙烯蜡等迁移析出，即产生吐霜现象。
技术实现思路
针对现有技术存在的不足，本专利技术的目的在于提供一种表面不粘结且不吐霜的哑光型软质TPU。为实现上述目的，本专利技术提供了如下技术方案：一种表面不粘结哑光型软质TPU，包括下述重量份：热塑性聚氨酯弹性体TPU：60份-80份消光剂：5份-20份相容剂：5份-10份防黏剂：5份...
【技术保护点】
1.一种表面不粘结哑光型软质TPU，其特征在于：包括下述重量份：热塑性聚氨酯弹性体TPU：60份‑80份消光剂：5份‑20份相容剂：5份‑10份防黏剂：5份‑10份抗氧剂：0.5份‑1份；所述防黏剂为2‑三甲基硅氧基‑4‑烯丙氧基二苯基酮、甲基三甲基硅基二甲基乙烯酮缩二乙醇、2，3，3，3‑四氟‑1‑丙烯、2‑丙烯酸‑2‑羧乙酯的混合物。
【技术特征摘要】
1.一种表面不粘结哑光型软质TPU，其特征在于：包括下述重量份：热塑性聚氨酯弹性体TPU：60份-80份消光剂：5份-20份相容剂：5份-10份防黏剂：5份-10份抗氧剂：0.5份-1份；所述防黏剂为2-三甲基硅氧基-4-烯丙氧基二苯基酮、甲基三甲基硅基二甲基乙烯酮缩二乙醇、2，3，3，3-四氟-1-丙烯、2-丙烯酸-2-羧乙酯的混合物。2.根据权利要求1所述的一种表面不粘结哑光型软质TPU，其特征在于：所述防黏剂为质量比为1～5∶0.5～2∶0.5～2∶0.8～3的2-三甲基硅氧基-4-烯丙氧基二苯基酮、甲基三甲基硅基二甲基乙烯酮缩二乙醇、2，3，3，3-四氟-1-丙烯、2-丙烯酸-2-羧乙酯的混合物。3.根据权利要求1所述的一种表面不粘结哑光型软质TPU，其特征在于：所述相容剂为HSB、SBS、SEBS、PE、PP为基材的MAH接枝物。4.根据权利要求1所述的一种表面不粘结哑光型软质TPU，其特征在于：所述相容剂为氢化苯乙烯-丁二烯-苯乙烯嵌段共聚物接枝马来酸酐聚合物。5.根据权利要求1所述的一种表面不粘结哑光型软质TPU，其特征在于：所述抗氧剂为抗氧剂1010、264或1076。6.根据权利要求1所述的一种表面不粘...