The invention provides a preparation method of waterborne phenolic epoxy resin emulsion and a coating composition containing it, and a preparation method of the waterborne phenolic epoxy resin emulsion. The method comprises the following steps: preparing liquid phenolic epoxy resin; dissolving the liquid phenolic epoxy resin in the 1.4 two oxygen six ring and heating it to 50 degree C, 70 degrees centigrade, then dripping into alcohol amine and heating up to 60 degrees 85 85 And 2 hours and 3 hours at constant temperature. After dropping to room temperature, glacial acetic acid is neutralized and salt is added, and water is added, so that waterborne phenolic epoxy resin emulsion is obtained. The waterborne phenolic epoxy resin emulsion has good water solubility and good stability, and its coating composition has good adhesion, impact strength, hardness and flexibility.
【技术实现步骤摘要】
水性酚醛环氧树脂乳液的制备方法及包含其的涂料组合物
本申请涉及涂料领域，具体地，涉及一种水性酚醛环氧树脂的制备方法及包含其的涂料组合物。
技术介绍
酚醛环氧树脂(EPN)化学名为线型酚醛多缩水甘醚油，浅棕黄色粘稠液体，是一种耐热型环氧树脂。由于酚醛环氧树脂结构中含有2个以上的环氧基团，环氧官能度高，可以与很多种类型的固化剂发生交联反应，形成三维网状结构，其固化物表现出优异的机械强度、电绝缘性能、耐水性、耐化学性、较高的玻璃化转变温度和热稳定性[1]。传统的酚醛环氧树脂涂料以有机溶剂作为分散剂，在生产和施工过程中会释放出大量的有毒有害气体到大气中，对环境和人类健康造成极大的危害，并且浪费大量的溶剂资源，已经不符合现代社会的环保要求。随着环保意识的增强，世界各国已经相继制定了严格的环境保护法规和政策，限制了挥发性有机化合物(VOC)的排放，使得传统的溶剂型涂料的发展越来越受到限制。
技术实现思路
为了解决上述问题，本专利技术提出一种水性酚醛环氧树脂乳液的制备方法及包含其的涂料组合物。一种水性酚醛环氧树脂乳液的制备方法，其包括如下步骤：制备液体酚醛环氧树脂；将上述液体酚醛环...
【技术保护点】
1.一种水性酚醛环氧树脂乳液的制备方法，其包括如下步骤：制备液体酚醛环氧树脂；将上述液体酚醛环氧树脂溶解于1.4‑二氧六环中并加热至50℃‑70℃，再滴入醇胺中并升温至60℃‑85℃，并恒温2‑3小时；降至室温后，滴加冰乙酸中和成盐，再加入水，即得到水性酚醛环氧树脂乳液。
【技术特征摘要】
2018.10.11 CN 20181118255041.一种水性酚醛环氧树脂乳液的制备方法，其包括如下步骤：制备液体酚醛环氧树脂；将上述液体酚醛环氧树脂溶解于1.4-二氧六环中并加热至50℃-70℃，再滴入醇胺中并升温至60℃-85℃，并恒温2-3小时；降至室温后，滴加冰乙酸中和成盐，再加入水，即得到水性酚醛环氧树脂乳液。2.如权利要求1所述的水性酚醛环氧树脂乳液的制备方法，其特征在于，所述制备液体酚醛环氧树脂的步骤包括：将苯酚与甲醛在稀盐酸的催化下于60~70℃反应0.8-1.2小时，减压除水后，在碱的作用下与环氧氯丙烷于80-120℃下反应1.2-1.8小时，去除溶剂得到所述液体酚醛环氧树脂。3.如权利要求1所述的水性酚醛环氧树脂乳液的制备方法，其特征在于，所述液体酚醛环氧树脂：醇胺：乙...
【专利技术属性】
技术研发人员：罗伟雄，
申请(专利权)人：东莞市山力高分子材料科研有限公司，
类型：发明
国别省市：广东,44