The invention discloses a production process of small-diameter wood filling board, which takes small-diameter wood core as raw material, passes through two-sided cutting, sizing, paving and hot pressing steps. The surface of the small-diameter wood filling board obtained by the production process of the invention is smooth and firm, the size stability of the base material is good, the ratio of qualified wood is high, the production cost is low, the utilization rate of small-diameter wood resources is high, and can meet the market demand of the product, and is healthy. The production process is simple and convenient for mass production, which is conducive to speeding up industrialization.
【技术实现步骤摘要】
小径木填充板的生产工艺
本领域属于人造板加工
，具体涉及一种小径木填充板的生产工艺。
技术介绍
本专利技术属于板材加工技术领目前小径圆材多是被粉碎后加工成密度板、刨花板或造纸用，传统加工过程中，尤其是胶合板生产过程旋切单板产生大量的木芯，由于直径较小，很难再进行加工利用。填充板板芯分布间距大，且含水率分布不均匀，极易在热压时出现板坯内的热传导不均匀，胶黏剂的固化程度不一致，进而破坏的板材尺寸的稳定性，导致翘曲、变形等质量问题。
技术实现思路
为解决以上现有技术问题，本专利技术提供一种小径木填充板的生产工艺，以小径木芯为原材料，经过两面裁切、施胶、铺板，热压得到小径木填充板表面平整结实，基材尺寸稳定性好，合格材比高，生产成本较低，小径木资源利用率高。本专利技术具体采用以下技术方案：小径木填充板的生产工艺，包括以下步骤：S1:选材：选取干燥后直径为28mm的小径木芯，进行两面裁切，得到方形木芯；S2:回湿：对方形木芯置于蒸房，设置蒸房温度为65-70℃，湿度为65-75%，待木芯含水率稳定，对木芯两个平面进行浸胶，将木芯铺于桉木单板进行铺板，得到板坯，室温晾放；S3...
【技术保护点】
1.小径木填充板的生产工艺，其特征在于，包括以下步骤：S1:选材：选取干燥后直径为28mm的小径木芯，进行两面裁切，得到方形木芯；S2:回湿：对方形木芯置于蒸房，设置蒸房温度为65‑70℃，湿度为65‑75%，待木芯含水率稳定，对木芯两个平面进行浸胶，将木芯铺于桉木单板进行铺板，得到板坯；S3:热压：修正板坯，置于热压机进行热压，热压温度为105‑115℃，压力为5‑6MPa，最后砂光板面，即得填充板成品。
【技术特征摘要】
1.小径木填充板的生产工艺，其特征在于，包括以下步骤：S1:选材：选取干燥后直径为28mm的小径木芯，进行两面裁切，得到方形木芯；S2:回湿：对方形木芯置于蒸房，设置蒸房温度为65-70℃，湿度为65-75%，待木芯含水率稳定，对木芯两个平面进行浸胶，将木芯铺于桉木单板进行铺板，得到板坯；S3:热压：修正板坯，置于热压机进行热压，热压温度为105-115℃，压力为5-6MPa，最后砂光板面，即得填充板成品。2.根据权利要求1所述的小径木填充板的生产工艺，其特征在于，步骤S1所述方形木芯两平面距离高度h为23mm。3.根据权利要求1所述的小径木填充板的生产工艺，其特征在于，步骤S2所述铺板过程，木芯间距为10-15mm。4.根据权利要求1所述的小径木填充板的生产工艺，其特征在于，所述热压...
【专利技术属性】
技术研发人员：黄祖善，
申请(专利权)人：南宁市邦得力木业有限责任公司，
类型：发明
国别省市：广西,45