The invention provides a preparation method of a long-life lithium-metal battery negative electrode and a lithium-metal battery; the invention takes metal lithium as the negative electrode, takes heterogeneous metal as the electrode, contains heterogeneous metal ions in the electrolyte, assembles a button battery, charges for a certain time under a small current, thus forming a heterogeneous metal film on the surface of the metal lithium negative electrode in situ, and the heterogeneous metal film can be used as the cathode. Stabilizing the interface between lithium metal and electrolyte can effectively inhibit the growth of lithium dendrite, reduce battery polarization, improve the rechargeability of lithium metal negative electrode, and then improve the performance of lithium metal battery. This method is simple and feasible, and has broad application prospects.
【技术实现步骤摘要】
一种长寿命锂金属电池负极制备方法及锂电池
本专利技术属于化学电源领域，也属于能源材料
具体涉及长寿命锂金属电池负极制备方法及长寿命锂金属电池负极制备方法及锂电池。
技术介绍
锂金属具有极高的理论比容量和极低的电化学电位，锂金属电池作为当今世界应用最广泛的和最有发展前景的电池之一，以锂金属为负极的锂空气电池和锂硫电池被认为是很有希望的下一代储能电池。然而，对于锂金属负极的实际应用，仍存在各种问题需要解决，其中最重要的是要解决电池充放电过程中金属锂表面的锂由于不均匀的沉积/溶解造成的锂枝晶的形成和生长。目前，常用的抑制锂枝晶的方法主要有：通过电解液添加剂或其他方法原位形成金属锂表面保护层、通过非原位方法制备保护层、改善集流体制备三维或其他形式的集流体，这些方法各自在一定程度上解决了锂金属负极在充放电循环过程中枝晶的生长问题，但又各自存在着一定的限制因素。最新研究进展表明，从构建锂复合负极的角度出发，可有效提高锂金属早充放电循环中的稳定性。合理的设计可以改变锂金属沉积偏好，从根本上改善锂枝晶生长的问题。然而对于绝大多数材料，其与锂金属之间的结合弱，即具有疏锂性。...
【技术保护点】
1.一种长寿命锂金属电池负极制备方法，其特征在于，金属锂片作为负极，异质金属作为对电极，电解液中含有异质金属盐；将金属锂片、对电极和电解液组装成扣式电池，以小电流恒定电流充电一定时间，使金属锂片表面原位生成一层异质金属层，所述异质金属层的厚度通过电流密度的大小和通电时间来控制；将所述扣式电池拆开，修饰后的金属锂片即为锂电池负极。
【技术特征摘要】
1.一种长寿命锂金属电池负极制备方法，其特征在于，金属锂片作为负极，异质金属作为对电极，电解液中含有异质金属盐；将金属锂片、对电极和电解液组装成扣式电池，以小电流恒定电流充电一定时间，使金属锂片表面原位生成一层异质金属层，所述异质金属层的厚度通过电流密度的大小和通电时间来控制；将所述扣式电池拆开，修饰后的金属锂片即为锂电池负极。2.如权利要求1所述的长寿命锂金属电池负极制备方法，其特征在于，所述电解液中含有可在金属锂表面稳定沉积的金属离子和溶剂。3.如权利要求2所述的长寿命锂金属电池负极制备方法，其特征在于，...
【专利技术属性】
技术研发人员：方聪聪，王勇，郭瑞，张亚莉，解晶莹，裴海娟，刘雯，李永，
申请(专利权)人：上海空间电源研究所，
类型：发明
国别省市：上海,31