The present invention relates to an electrophoretic post-treatment process for aluminium and aluminium alloys for automobile decoration, which belongs to the field of electrophoretic post-treatment technology. It mainly includes the following steps: first, three reverse osmosis washing processes are carried out on aluminium alloy parts after electrophoretic treatment, then baking, then hot water treatment, and finally drying. The invention adopts a multi-channel continuous and closed reverse osmosis water washing circulating system, removes the floating paint on the surface of the product, makes the surface of the alloy parts more smooth and smooth, greatly saves water consumption and water resources, and uses hot water boiling process to fundamentally eliminate the phenomenon of the alloy parts whitening in water.
【技术实现步骤摘要】
一种汽车装饰用铝及铝合金电泳的后处理工艺
本专利技术属于电泳后处理
，具体涉及一种汽车装饰用铝及铝合金电泳的后处理工艺。
技术介绍
铝合金具有比强度高，良好的导热和导电性、反光性强、塑形好、成型性好、无低温脆性、加工性能好、抗大气腐蚀能力强、易于成型、价格便宜等优点，被广泛应用于现代汽车制造业及建材行业。尤其是对铝及铝合金电泳表面处理后，铝及铝合金工件具有了相对传统阳极氧化更强的耐磨性、耐腐蚀性、耐碱性。电泳工艺在引入到汽车外饰件行业后，产生了先阳极氧化再涂覆一层电泳漆膜的新型工艺，使得铝及铝合金材料不但具有较强的耐腐蚀性，同时也具有了传统氧化一样高亮、绚丽的外观。合金工件的表面处理工艺种类繁多，工序也需要根据工件性质进行调整。虽然目前的阳极氧化与电泳工艺均已较为成熟，但是很多人却忽视了部分缺陷。电泳工艺中，由于电泳过程中电渗透不充分导致水吸附在氧化膜孔内，再经过固化电泳膜后，遇水产品的表面会出现发白的现象，严重影响产品外观。如公开号105408429A的专利公开了在固化前用水性溶胶-凝胶组合物后处理浸渍漆涂层的浸渍漆涂布导电基材的方法，即在固化前采用水性溶...
【技术保护点】
1.一种汽车装饰用铝及铝合金电泳的后处理工艺，其特征在于，所述的后处理工艺包括如下步骤：将电泳处理后的铝合金件先进行三道反渗透水洗处理，然后烘烤，接着再进行热水处理，最后干燥。
【技术特征摘要】
1.一种汽车装饰用铝及铝合金电泳的后处理工艺，其特征在于，所述的后处理工艺包括如下步骤：将电泳处理后的铝合金件先进行三道反渗透水洗处理，然后烘烤，接着再进行热水处理，最后干燥。2.根据权利要求1所述的汽车装饰用铝及铝合金电泳的后处理工艺，其特征在于，所述热水处理具体为：将铝合金件直接浸入温度为70-100℃的热水中，恒温水煮10-50min。3.根据权利要求1所述的汽车装饰用铝及铝合金电泳的后处理工艺，其特征在于，所述三道反渗透水洗为闭合循环系统。4.根据权利要求1或3所述的汽车装饰用铝及铝合金电泳的后处理工艺，其特征在于，所述三道反渗透水洗的时间依次为：40-90s；50-150s；40-90s。5.根据权利要求1所述的汽车装...
【专利技术属性】