The invention relates to an insulating and wear-resistant coating for electric rope grabbers and a preparation method thereof, belonging to the technical field of coatings for electrical products. The insulating and wear-resistant coating for electric power rope grabber comprises the following raw materials: organic silicone resin 30_50, polysiloxane 15_30, zirconia 4_6, silicon nitride 1_2, silica sol 3_10, ethyl acetate 15_20, rosin glyceride 1_2, inorganic filler 5_10, wetting dispersant 1_5, propylene glycol methyl ether acetate 2_3. The invention provides a simple and practical preparation method of an insulating and wear-resistant coating for electric rope grabbers, which has simple formula, scientific design, excellent electrical insulation, wear resistance and aging resistance.
【技术实现步骤摘要】
电力抓绳器用绝缘耐磨涂料及其制备方法
本专利技术涉及一种电力抓绳器用绝缘耐磨涂料及其制备方法,属于电工产品用涂料
技术介绍
电力行业所用的抓绳器种类繁多,不但要求其具有优异的电绝缘性,而且由于长期室外作业,对抓绳器的耐老化性能和耐磨性能要求也比较高。现有的方法就是涂覆一层保护层,但是保护层的质量无法满足以上性能要求。
技术实现思路
本专利技术的目的是提供一种电力抓绳器用绝缘耐磨涂料,其配方简单、设计科学,具有优异的电绝缘性、耐磨性和耐老化性;同时本专利技术提供了一种简单实用的电力抓绳器用绝缘耐磨涂料的制备方法。所述电力抓绳器用绝缘耐磨涂料,包括以下重量份数的原料:有机硅树脂30-50份,聚硅醚15-30份,氧化锆4-6份,氮化硅1-2份,硅溶胶3-10份,乙酸乙酯15-20份,松香甘油酯1-2份,无机填料5-10份,润湿分散剂1-5份,丙二醇甲醚醋酸酯2-3份。所述有机硅树脂具有优异的电绝缘性和热氧化稳定性。所述的聚硅醚不但具有优异的电绝缘性和防腐蚀性。所述的氧化锆和氮化硅,由于两者特殊的性能,提高了涂料的耐磨性。所述无机填料的平均粒径为5-8μm。无机填料为碳酸钙、钛白粉、高岭土或者云母粉。所述的电力抓绳器用绝缘耐磨涂料的制备方法,先将有机硅树脂和聚硅醚混合,再将混合物加入到50-70℃的乙酸乙酯中搅拌,然后将氧化锆、氮化硅、硅溶胶和松香甘油酯加入到乙酸乙酯中,最后加入无机填料、润湿分散剂和丙二醇甲醚醋酸酯,在2000-2500转/分下继续搅拌反应20-40分钟,研磨得到浆料,即得电力抓绳器用绝缘耐磨涂料。所述电力抓绳器用绝缘耐磨涂料中,有机硅树脂 ...
【技术保护点】
1.一种电力抓绳器用绝缘耐磨涂料,其特征在于包括以下重量份数的原料:有机硅树脂30‑50份,聚硅醚15‑30份,氧化锆4‑6份,氮化硅1‑2份,硅溶胶3‑10份,乙酸乙酯15‑20份,松香甘油酯1‑2份,无机填料5‑10份,润湿分散剂1‑5份,丙二醇甲醚醋酸酯2‑3份。
【技术特征摘要】
1.一种电力抓绳器用绝缘耐磨涂料,其特征在于包括以下重量份数的原料:有机硅树脂30-50份,聚硅醚15-30份,氧化锆4-6份,氮化硅1-2份,硅溶胶3-10份,乙酸乙酯15-20份,松香甘油酯1-2份,无机填料5-10份,润湿分散剂1-5份,丙二醇甲醚醋酸酯2-3份。2.根据权利要求1所述的电力抓绳器用绝缘耐磨涂料,其特征在于:无机填料的平均粒径为5-8μm。3.根据权利要求2所述的电力抓绳器用绝缘耐磨涂料,...