The present invention discloses a high temperature and corrosion resistant coating for color steel plate, which is made of 5 7 parts of dimethyl ethanolamine, 7 9 parts of butanediol, 20 25 parts of polyamide resin, 5 6 parts of talc powder, 3 4 parts of tributyl phosphate, 5 8 parts of methanol, 4 6 parts of sodium hydroxymethyl cellulose, 7 9 parts of bentonite, 1 2 parts of polytetrafluoroethylene, 8 10 parts of zinc carbonate, 5 parts of chromium chloride. 7 copies. The invention has good high temperature resistance, strong corrosion resistance, strong adhesion force, no shedding and cracking, and can effectively prevent the cracking and shedding of the adhesion layer of color plate steel and prevent the occurrence of corrosion.
【技术实现步骤摘要】
一种彩钢板耐高温防腐蚀涂料
本专利技术涉及钢材防护
,尤其涉及一种彩钢板耐高温防腐蚀涂料。
技术介绍
彩板刚在使用过程中,常常会暴晒在烈日底下,高温造成油漆等粘附层开裂脱落,且由于雨水等腐蚀性物质对其表面的腐蚀,致使彩板刚表面生锈,导致彩板刚强度降低,影响正常使用。
技术实现思路
为解决上述存在的问题,本专利技术提供一种耐高温性好,防腐蚀能力强,粘着力强,无脱落无开裂的彩钢板耐高温防腐蚀涂料。本专利技术解决上述技术问题采用的技术方案为:一种彩钢板耐高温防腐蚀涂料,由以下质量份数的原料制成:二甲基乙醇胺5-7份,丁二醇7-9份,聚酰胺树脂20-25份,滑石粉5-6份,磷酸三丁酯3-4份,甲醇5-8份,羟甲基纤维素钠4-6份,膨润土7-9份,聚四氟乙烯1-2份、碳酸锌8-10份,氯化铬5-7份。上述的彩钢板耐高温防腐蚀涂料,由以下质量份数的原料制成:二甲基乙醇胺6份,丁二醇8份,聚酰胺树脂23份,滑石粉5.4份,磷酸三丁酯3.5份,甲醇7份,羟甲基纤维素钠5份,膨润土8份,聚四氟乙烯1.7份、碳酸锌9份,氯化铬6份。本专利技术解决技术问题所带来的有益效果在于:本专利技术耐高温性好,防腐蚀能力强,粘着力强,无脱落无开裂,能有有效防止彩板钢粘附层开裂脱落,防止腐蚀的发生。具体实施方式下面结合具体实施例对本专利技术做进一步详细说明。实施例1一种彩钢板耐高温防腐蚀涂料,由以下质量份数的原料制成:二甲基乙醇胺5份,丁二醇7份,聚酰胺树脂20份,滑石粉5份,磷酸三丁酯3份,甲醇5份,羟甲基纤维素钠4份,膨润土7份,聚四氟乙烯1份、碳酸锌8份,氯化铬5份。实施例2一种彩钢 ...
【技术保护点】
1.一种彩钢板耐高温防腐蚀涂料,其特征在于:由以下质量份数的原料制成:二甲基乙醇胺5‑7份,丁二醇7‑9份,聚酰胺树脂20‑25份,滑石粉5‑6份,磷酸三丁酯3‑4份,甲醇5‑8份,羟甲基纤维素钠4‑6份,膨润土7‑9份,聚四氟乙烯1‑2份、碳酸锌8‑10份,氯化铬5‑7份。
【技术特征摘要】
1.一种彩钢板耐高温防腐蚀涂料,其特征在于:由以下质量份数的原料制成:二甲基乙醇胺5-7份,丁二醇7-9份,聚酰胺树脂20-25份,滑石粉5-6份,磷酸三丁酯3-4份,甲醇5-8份,羟甲基纤维素钠4-6份,膨润土7-9份,聚四氟乙烯1-2份、碳酸锌8-10份,氯化铬...
【专利技术属性】
技术研发人员:吕淑敏,
申请(专利权)人:青岛海大智汇科技管理咨询有限公司,
类型:发明
国别省市:山东,37