The invention discloses a method for extracting and purifying ferrous, which comprises the following steps: (1) adding dilute sulfuric acid to the waste liquid containing iron, adjusting the pH to 2-3, stirring the reaction for 20-40 minutes at 60-90 (?) filtering the reaction solution, collecting the filtrate, then adding a reductant to the filtrate, and reducing it for 1-5 hours at 45-60 (?) returning the obtained step (1) The solution of the original reaction is filtered, filtrate is collected, organic solvent is added to the filtrate, recrystallization is carried out at 2-3 ~C, ferrous sulfate crystal is prepared, and then freeze-drying is carried out to prepare the ferrous sulfate. The invention deals with the wastewater containing iron to prepare ferrous sulfate, and achieves the recovery and utilization of resources.
【技术实现步骤摘要】
一种亚铁的提取提纯方法
本专利技术涉及含铁废水的回收利用，尤其是涉及一种通过氧化还原及重结晶反应制备硫酸亚铁的方法。
技术介绍
随着世界大环境的污染情况，人们对环境保护越来越重视，减少工业废水的排放或对工业废水进行二次利用，以解决化学工业对环境的污染。铁元素主要是以氧化产物的形式作为废料排除，每年用于氧化铁的原料使用很多，这样造成大量资源的浪费；同时如果将铁元素采用就地掩埋或者堆放的处理方式，这样就会占用土地或污染地下水资源，这样更不利于环境保护。
技术实现思路
针对现有技术存在的上述问题，本专利技术申请人提供了一种亚铁的提取提纯方法。本专利技术对含铁废水进行处理，制备硫酸亚铁，做到了资源的回收利用。本专利技术的技术方案如下：一种亚铁的提取提纯方法，所述方法包括如下步骤：(1)在含铁废液中加入稀硫酸，调节pH为2～3，在60～90℃条件下搅拌反应20～40min；(2)对反应溶液进行过滤，收集滤液，之后向滤液中加入还原剂，并在45～60℃条件下还原1～5h；(3)对步骤(1)所得的经过还原反应的溶液进行过滤，收集滤液，向滤液中加入有机溶剂，在-2～3℃条件下重结晶，制...
【技术保护点】
1.一种亚铁的提取提纯方法，其特征在于，所述方法包括如下步骤：(1)在含铁废液中加入稀硫酸，调节pH为2～3，在60～90℃条件下搅拌反应20～40min；(2)对反应溶液进行过滤，收集滤液，之后向滤液中加入还原剂，并在45～60℃条件下还原1～5h；(3)对步骤(1)所得的经过还原反应的溶液进行过滤，收集滤液，向滤液中加入有机溶剂，在‑2～3℃条件下重结晶，制得硫酸亚铁晶体，之后冷冻干燥，制得所述亚铁。
【技术特征摘要】
1.一种亚铁的提取提纯方法，其特征在于，所述方法包括如下步骤：(1)在含铁废液中加入稀硫酸，调节pH为2～3，在60～90℃条件下搅拌反应20～40min；(2)对反应溶液进行过滤，收集滤液，之后向滤液中加入还原剂，并在45～60℃条件下还原1～5h；(3)对步骤(1)所得的经过还原反应的溶液进行过滤，收集滤液，向滤液中加入有机溶剂，在-2～3℃条件下重结晶，制得硫酸亚铁晶体，之后冷冻干燥，制得所述亚铁。2.根据权利要求1所述的方法，其特征在...
【专利技术属性】
技术研发人员：姚世明，
申请(专利权)人：无锡日月水处理有限公司，
类型：发明
国别省市：江苏,32