The invention discloses a preparation method of cubic lightweight calcium carbonate filler, which comprises the following steps: taking calcium hydroxide semen and fully carbonizing it to obtain mature slurry as mother liquor; adding crystal form control agent into calcium hydroxide semen to compose mixed liquor; slowly dropping the mixed liquor into the mother liquor while carbonizing, while dropping the upper part of the reactor at the same flow rate at the bottom of the reactor. At the same time, the cubic light calcium carbonate filler is obtained after carbonization to the end point. The cubic lightweight calcium carbonate filler prepared by the invention has a specific surface area of 2.0 4.5m.
【技术实现步骤摘要】
一种立方体轻质碳酸钙填料的制备方法
本专利技术涉及造纸填料制备领域，具体涉及一种立方体轻质碳酸钙填料的制备方法。
技术介绍
轻质碳酸钙是造纸工业中最常用的填料之一，用填料替代造纸纤维，可以降低生产成本，另外可以改善纸张的光学性能、印刷性能和外观。轻质碳酸钙作为一种重要的无机化工原料，用普通碳化法生产出的轻质碳酸钙，多为纺锤型或针棒状，粒径分布范围宽，比表面积较大；另外，通过添加助剂及控制反应条件可以制得的纳米级轻质碳酸钙晶型多为立方体，一般小于100nm，具有很高的比表面积，容易团聚，通常不能直接用于造纸加填。填料的比表面积与其粒径、粒径分布和粒子形状有关。大多数填料的粒径和比表面积之间存在着相反的关系。一般来说，粒径越小，比表面积越大。较高比表面积的填料较难留着。相对于纤维，填料有更高的比表面积，单位质量填料比纤维具有更大的吸附湿部添加剂的能力，所以高比表面积填料要求更多的助留剂以达到一定的留着程度。填料的比表面积还影响光散射，也影响纸页强度和印刷特性。一般来说，较高比表面积的填料可以提高纸张印刷性能(如油墨吸收等)，但同时也会影响填料的留着，造成添加剂的选择性...
【技术保护点】
1.一种立方体轻质碳酸钙填料的制备方法，其特征在于，包括如下步骤：步骤一，取氢氧化钙精浆，充分碳化从而获得熟浆作为母液；步骤二，将晶型控制剂加入氢氧化钙精浆中配成混合液；步骤三，将所述混合液缓慢滴加入所述母液中，同时进行碳化，上部滴加的同时反应器底部以相同流速同时出料，碳化至终点后得到所述立方体轻质碳酸钙填料。
【技术特征摘要】
1.一种立方体轻质碳酸钙填料的制备方法，其特征在于，包括如下步骤：步骤一，取氢氧化钙精浆，充分碳化从而获得熟浆作为母液；步骤二，将晶型控制剂加入氢氧化钙精浆中配成混合液；步骤三，将所述混合液缓慢滴加入所述母液中，同时进行碳化，上部滴加的同时反应器底部以相同流速同时出料，碳化至终点后得到所述立方体轻质碳酸钙填料。2.如权利要求1所述的方法，其特征在于，所述晶型控制剂为碳酸盐或碳酸氢盐的一种或两种以上。3.如权利要求2所述的方法，其特征在于，所述晶型控制剂选自碳酸钠、碳酸氢钠、碳酸钾或碳酸氢钾。4.如权利要求1所述的方法，其特征在于，所述氢氧化钙精浆中氢氧化钙的粒径小于80目。5.如权利要求1所述的方法，其特征在于，步骤三中，通过在线测定体系的电导率和pH值控制滴加速度和出料速度。6.如权利要求5所述的方法，其特征在于，所述电导率控制在0.5-2.5ms/cm，pH值控制在8-...
【专利技术属性】
技术研发人员：施晓旦，刘莹，傅斌，
申请(专利权)人：东升新材料山东有限公司，
类型：发明
国别省市：山东,37