一种调节溶剂配比获得形貌可控微纳米二氧化铈的方法技术

本发明专利技术公开了一种调节溶剂配比获得形貌可控微纳米二氧化铈的方法。以CeCl3·7H2O为铈源，以氨水或氢氧化钠为碱，以乙二醇和水为溶剂，通过调节乙二醇和水的配比溶剂热法合成形貌可控的前驱体，将前驱体煅烧得到保持原有形貌的微纳米二氧化铈。该方法操作简单，得到的空心柱状二氧化铈结构新颖。

A method for obtaining morphologically controllable micro-and nano-ceria by adjusting the solvent ratio

The invention discloses a method for obtaining micro and nano ceria with controllable morphology by adjusting the solvent ratio. Using CeCl3.7H_2O as cerium source, ammonia or sodium hydroxide as alkali, ethylene glycol and water as solvents, the morphology-controllable precursors were synthesized by solvent-thermal method by adjusting the ratio of ethylene glycol and water. The precursors were calcined to obtain micro-and nano-ceria with the original morphology. The method is simple to operate and the hollow cylindrical cerium dioxide structure obtained is novel.

【技术实现步骤摘要】
一种调节溶剂配比获得形貌可控微纳米二氧化铈的方法
本专利技术属于微纳米材料制备
，涉及一种调节溶剂配比获得形貌可控微纳米二氧化铈的方法。
技术介绍
CeO2是一种重要的稀土功能材料，具有优良的氧离子传输能力，在催化、发光、紫外吸收、固体氧化物燃料电池、抛光等诸多领域有着广泛应用。纳米尺度下CeO2相对于体相材料，电子结构发生改变，比表面积增大，往往表现出一些新的物理性质和更高的化学活性。纳米材料的性能，除了取决于材料的化学组成、结晶学结构外，还与纳米晶体的大小、形状、表面结构以及生长方向、聚集状态等相关。因此，发展尺寸和形貌可控的CeO2纳米材料的制备方法成为研究热点。水(溶剂)热合成是在高温高压条件下，溶剂处于临界或超临界状态下进行的合成反应；具有生成产物分散性好、纯度高、形貌可控等优点。近年来，围绕铈基纳米材料的水(溶剂)热合成开展了大量研究，通过控制合成参数可以实现对产物尺寸和形状的调节。例如，HaoxinMai等(J.Phys.Chem.B，2005，109，24380-24385)以硝酸铈和氢氧化钠为原料水热合成纳米CeO2，通过控制氢氧化钠浓度制备了CeO2多面体、本文档来自技高网...

【技术保护点】
1.一种调节溶剂配比获得形貌可控微纳米二氧化铈的方法，其特征在于，具体包括如下步骤：(1)将CeCl3·7H2O溶于乙二醇或乙二醇/水混合溶液，搅拌条件下滴加一定浓度的碱溶液，得到反应液，将反应液转移至反应釜内，在140～220℃恒温反应12～24h，反应完毕后对固体产物进行离心分离、洗涤干燥，得到前驱体；(2)将前驱体在600℃煅烧1～4h，得到微纳米二氧化铈。

【技术特征摘要】
1.一种调节溶剂配比获得形貌可控微纳米二氧化铈的方法，其特征在于，具体包括如下步骤：(1)将CeCl3·7H2O溶于乙二醇或乙二醇/水混合溶液，搅拌条件下滴加一定浓度的碱溶液，得到反应液，将反应液转移至反应釜内，在140～220℃恒温反应12～24h，反应完毕后对固体产物进行离心分离、洗涤干燥，得到前驱体；(2)将前驱体在600℃煅烧1～4h，得到微纳米二氧化铈。2.如权利要求1所述的一种调节溶剂配比获得形貌可控微纳米二氧化铈的方法，其特征在于，步骤(1)中所述碱溶液为氨或氢氧...

【专利技术属性】
技术研发人员：李静，王春波，吴婷，郭桂花，李永绣，
申请(专利权)人：南昌大学，
类型：发明
国别省市：江西,36