金属粉末层压造形用的金属粉末材料制造技术

预提供在金属粉末层压造形中生成马氏体时效钢的三维造形物的、不含钴的金属粉末材料。金属粉末材料包含：铁76重量％以上、碳0.03重量％以下、硅0.12％重量以下、锰0.12重量％以下、镍17重量％以上且19重量％以下、钼1.5重量％以上且2.5重量％以下、钛0.5重量％以上且2.0重量％以下、铝1.5重量％以下且包括0重量％，剩余部分为不可避免地混入的杂质，杂质的含量为每种杂质均不足0.01重量％。因此，在时效处理后，由本发明专利技术的金属粉末材料制备的三维造形物具有马氏体时效钢的特性，并且具有足够高的硬度及相对高的拉伸强度。

Metal Powder Materials for Laminating Metal Powder

A three-dimensional maraging steel, cobalt-free metal powder material, is provided in advance for the formation of maraging steel in metal powder lamination. Metal powder materials include: iron 76%, carbon 0.03%, silicon 0.12%, manganese 0.12%, nickel 17% and 19%, molybdenum 1.5% and 2.5%, titanium 0.5% and 2.0%, aluminium 1.5% and less than 0%. The remaining parts are inevitably mixed impurities. The content of impurities is less than 0.01 weight per impurity. Therefore, after aging treatment, the three-dimensional shape formed by the metal powder material of the present invention has the characteristics of maraging steel, and has high enough hardness and relatively high tensile strength.

【技术实现步骤摘要】
金属粉末层压造形用的金属粉末材料
本专利技术涉及一种金属粉末层压造形用的金属粉末材料。尤其，本专利技术涉及一种用以生成相当于马氏体时效钢(maragingsteel)的铁制的三维造形物的金属粉末材料。
技术介绍
已知有对金属粉末材料照射激光或电子束来生成期望的三维造形物的金属粉末层压造形法。可以说，只要是可在常温下作为粉体而存在，并且可在由激光或电子束熔融并进行冷却而凝固之后，在常温下作为固体而存在的金属元素，则基本上均可用作金属粉末层压造形用的金属粉末材料。作为适合于金属粉末层压造形的金属粉末材料，实际上使用的是与马氏体时效钢相同组成的金属粉末材料。例如，在专利文献1中，具体揭示了含有17重量％以上且19重量％以下的镍的18镍(Ni)系马氏体时效钢、及去除钴及钼而含有19重量％以上且20重量％以下的镍的20Ni系马氏体时效钢的金属粉末层压造形用的金属粉末材料的组成。例如，18Ni系马氏体时效钢中，作为对于获得时效处理后所要求的硬度或拉伸强度来说不可或缺的元素，含有7重量％以上且13重量％以下的钴、3重量％以上且5重量％以下的钼、0.2重量％以上且2重量％以下的钛、0.5重量％以上且本文档来自技高网...

【技术保护点】
1.一种金属粉末层压造形用的金属粉末材料，其特征在于，通过对由以下成分组成的多种合金的粉体进行混合而成；76重量％以上的铁Fe，0.03重量％以下的碳C，0.12重量％以下的硅Si，0.12重量％以下的锰Mn，17重量％以上且19重量％以下的镍Ni，1.5重量％以上且2.5重量％以下的钼Mo，0.5重量％以上且2.0重量％以下的钛Ti，1.5重量％以下的铝Al，剩余部分为不足0.01重量％、不可避免地混入的杂质。

【技术特征摘要】
2017.10.13 JP 2017-1992181.一种金属粉末层压造形用的金属粉末材料，其特征在于，通过对由以下成分组成的多种合金的粉体进行混合而成；76重量％以上的铁Fe，0.03重量％以下的碳C，0....

【专利技术属性】
技术研发人员：真家信夫，
申请(专利权)人：株式会社沙迪克，
类型：发明
国别省市：日本,JP